Materials for Marine Systems and StructuresDennis F. Hasson, C. Robert Crowe |
From inside the book
Results 1-3 of 91
Page 135
... Temperature The effect of temperature on the corrosion of metals is complicated by the interdependence of other relevant parameters and temperature . The kinetics of activation - controlled oxidation reactions and diffusion - controlled ...
... Temperature The effect of temperature on the corrosion of metals is complicated by the interdependence of other relevant parameters and temperature . The kinetics of activation - controlled oxidation reactions and diffusion - controlled ...
Page 222
... Temperature Data compiled from several studies on the erosion - corrosion of copper- base alloys at different temperatures show a mixed trend with regard to the effect of temperature on the erosion - corrosion rate ( 327 ) . The rate ...
... Temperature Data compiled from several studies on the erosion - corrosion of copper- base alloys at different temperatures show a mixed trend with regard to the effect of temperature on the erosion - corrosion rate ( 327 ) . The rate ...
Page 393
... temperature T ( ° C ) can be estimated by the following equation : where T ̧ = T + 30 + T , + Ti + T , + Ts + Tq + T2 , Tis the thickness temperature adjustment . It can be taken as 0 ° C for a thickness of 20 mm , -20 ° C for 30 mm ...
... temperature T ( ° C ) can be estimated by the following equation : where T ̧ = T + 30 + T , + Ti + T , + Ts + Tq + T2 , Tis the thickness temperature adjustment . It can be taken as 0 ° C for a thickness of 20 mm , -20 ° C for 30 mm ...
Other editions - View all
Common terms and phrases
AISI aluminum alloys anode applications Austenitic Austenitic cast iron bacteria biofilm biofouling bronze C(PR carbon steel cathodic protection chemical chlorine coatings composition concentration concrete copper alloys corrosion behavior corrosion rates corrosion resistance crevice attack crevice corrosion decrease deep ocean dissolved oxygen effect Engineering erosion-corrosion exposure factors failure fatigue film fouling fracture control galvanic corrosion galvanic coupling galvanic series heat treatment high strength HSLA hydrogen immersed increased inspection intergranular intergranular corrosion ions joints loading low alloy steels macrofouling marine atmospheres marine environments marine structures Martensitic materials maximum mechanical microbial microorganisms Naval nickel North Sea occur offshore platforms Offshore Structures organisms oxidation oxygen content P(PR Pacific Ocean polluted prestressed Reinhart ropes S-N curve salinity seawater selection ship shown in Figure specimens stainless steels Stress Corrosion Cracking sulfide Table temperature tests tide zone titanium alloys Type velocity weight weld wind zinc
References to this book
Fatigue in Composites: Science and Technology of the Fatigue Response of ... Bryan Harris Limited preview - 2003 |