Page 49
... static mechanical measurements are summarized in Table 11 . Table 11. Healing conditions and static mechanical data for welded PET samples [ 168 ] Healing temperature ( ° C ) for 140 160 180 200 220 240 250 24 hr duration Stress at ...
... static mechanical measurements are summarized in Table 11 . Table 11. Healing conditions and static mechanical data for welded PET samples [ 168 ] Healing temperature ( ° C ) for 140 160 180 200 220 240 250 24 hr duration Stress at ...
Page 306
... static or monotonic loading . The difference between the FCP response of T- and L - notched specimens should depend first on the relative layer thickness ( in this case namely 2S / B > C / B ) and second on the relative fiber ...
... static or monotonic loading . The difference between the FCP response of T- and L - notched specimens should depend first on the relative layer thickness ( in this case namely 2S / B > C / B ) and second on the relative fiber ...
Page 314
... static and cyclic loading were emphasized . Fatigue resistance of PA's as a function of water content goes through a maximum , which is attributed to a change in kind of water bonding . It was claimed that FCP behavior both of unfilled ...
... static and cyclic loading were emphasized . Fatigue resistance of PA's as a function of water content goes through a maximum , which is attributed to a change in kind of water bonding . It was claimed that FCP behavior both of unfilled ...
Contents
SOLID STATE REACTIONS IN LINEAR | 1 |
TRANSREACTIONS AND POSTADDITIONAL | 19 |
CHEMICAL HEALING | 43 |
Copyright | |
21 other sections not shown
Other editions - View all
Common terms and phrases
acid additional solid amorphous annealing Appl aspect ratio behavior birefringence block temperature chain Chem chemical healing composites copolyester copolymer courtesy crystallinity crystallization curves decreases deformation degree of crystallinity density diameter diffusion domains effect Equation exchange reactions extrusion temperature Fakirov fiber axis fibers drawn filament fracture mechanics fracture toughness function heat of fusion heated element higher increasing initial kg/cm² kinetics linear polycondensates macromolecules Makromol material matrix maximum measurements mechanical melting point microfibrils microstructure mm/min modulus molding molecules morphology nominal draw ratio noncrystalline nylon 6 fibers nylon 66 orientation parameters peak PET fibers phase Phys polyamides polyesters Polymer Sci polymerization properties Reprinted from Ref samples SAXS Schultz semicrystalline shown in Figure solid state polycondensation solid state post-polycondensation solid state reactions Solid-state extrusion specimen spherulite strength stress structure Table tensile terephthalate thermoplastics toughened transesterification transreactions values x-ray yield Zachmann