... Toughening Incorporation of submicron elastomeric particles is a useful tool to upgrade the toughness and impact resistance of polymers . This may be carried out either during the polymerization ( e.g. , [ 27–29 ] ) , or subsequently by ...
... Toughening Incorporation of submicron elastomeric particles is a useful tool to upgrade the toughness and impact resistance of polymers . This may be carried out either during the polymerization ( e.g. , [ 27–29 ] ) , or subsequently by ...
Page 263
... Toughening In the literature , standardized impact strength values ( Charpy , Izod ) are often available for particle - toughened engineering thermoplastics such as PA - 6 [ 28-29 , 77-78 ] , PA - 6.6 [ 28-29 , 79-80 ] , PET [ 81 ] ...
... Toughening In the literature , standardized impact strength values ( Charpy , Izod ) are often available for particle - toughened engineering thermoplastics such as PA - 6 [ 28-29 , 77-78 ] , PA - 6.6 [ 28-29 , 79-80 ] , PET [ 81 ] ...
Page 267
... toughened PBT and PBT / PC blends shear deforma- tion is the major toughening mechanism . In the former system this process is accompanied again by the internal cavitation of the impact modifier [ 86 ] . H 10 um 3.2.2 . Composites It ...
... toughened PBT and PBT / PC blends shear deforma- tion is the major toughening mechanism . In the former system this process is accompanied again by the internal cavitation of the impact modifier [ 86 ] . H 10 um 3.2.2 . Composites It ...
Contents
SOLID STATE REACTIONS IN LINEAR | 1 |
CHEMICAL HEALING | 43 |
PRACTICAL ASPECTS OF ADDITIONAL SOLID STATE | 59 |
Copyright | |
19 other sections not shown
Other editions - View all
Common terms and phrases
acid additional solid amorphous annealing Appl aspect ratio behavior birefringence block temperature chain Chem composites copolyester copolymer courtesy crystallinity crystallization curves decreases deformation degree of crystallinity density diameter diffusion domains Dröscher effect Equation exchange reactions extrusion temperature Fakirov fiber axis fibers drawn filament fracture mechanics fracture toughness function heat of fusion heated element higher increasing initial kg/cm² kinetics linear polycondensates load macromolecules Makromol material matrix maximum measurements mechanical melting point microfibrils microstructure mm/min modulus molded molecules morphology nominal draw ratio noncrystalline nylon 6 fibers nylon 66 orientation parameters peak PET fibers phase Phys polyamides polyesters Polymer Sci polymerization properties Reprinted from Ref samples SAXS Schultz semicrystalline shown in Figure solid state polycondensation solid state post-polycondensation solid state reactions Solid-state extrusion specimen spherulite strength stress structure Table tensile terephthalate thermoplastics toughened transesterification transreactions values x-ray yield Zachmann