... DMDHEU formulations ( such as Hylite LF * ) , this usually requires careful control during processing . However , preliminary experiments conducted by NeutraTherm Co. [ 3 ] and us indicated that fabrics containing at least 5 ...
... DMDHEU formulations ( such as Hylite LF * ) , this usually requires careful control during processing . However , preliminary experiments conducted by NeutraTherm Co. [ 3 ] and us indicated that fabrics containing at least 5 ...
Page 422
... DMDHEU blend . All fabrics cured 3 min / 90 ° C had acceptable weight gains [ 31-47 % for those treated with the unalkylated DMDHEU ( Table I ) and 30-38 % for those treated with the blended DMDHEU ( Table II ) ] . Fabrics cured at 100 ...
... DMDHEU blend . All fabrics cured 3 min / 90 ° C had acceptable weight gains [ 31-47 % for those treated with the unalkylated DMDHEU ( Table I ) and 30-38 % for those treated with the blended DMDHEU ( Table II ) ] . Fabrics cured at 100 ...
Page 427
... DMDHEU / PEG - 1000 , cured 3 min / 90 ° C ) showing location of polymer . resin resulted in stiffness values for treated 35/65 cotton / polyester and all cotton fabrics that were equivalent to the corresponding control fabrics only ...
... DMDHEU / PEG - 1000 , cured 3 min / 90 ° C ) showing location of polymer . resin resulted in stiffness values for treated 35/65 cotton / polyester and all cotton fabrics that were equivalent to the corresponding control fabrics only ...
Contents
Technological Developments in ManMade Fibers and Related | 33 |
Morphology and Near Tm Behavior of High Performance Ultrahigh | 67 |
Properties Structures and Temperature Limitations | 87 |
Copyright | |
22 other sections not shown
Common terms and phrases
amorphous analysis angle appear Applied assumed behavior bending birefringence blend braided break calculated carpet compared composite compression constant cotton crystalline crystallization curve decrease deformation density dependence described determined developed diameter diffusion direction discussed distance distribution draw effect energy experimental extension fabric factor failure fiber filament finish force fraction function geometry given heat higher impact improved increase indicated initial length liquid load lower m/min material measured mechanical method modulus nylon observed obtained occur orientation parameters phase polyester polymer possible present pressure produced properties range ratio recovery relative sample Scanning shape shear shown in Figure shows solution specimen Spectra speed spinning spun strain strength stress structure surface Table temperature tenacity tensile Text treated treatment twist unit values variability yarn