COLD DRAWING MODEL Experimental Cells A-D from Table I were cold drawn
at ASTM ambient conditions on the Instron at a strain rate of 100%/min. Four
draw ratios per cell were selected to represent nominal draw factors of 0.2, 0.4,
0.6, ...
COLD DRAWING MODEL Experimental Cells A-D from Table I were cold drawn
at ASTM ambient conditions on the Instron at a strain rate of 100%/min. Four
draw ratios per cell were selected to represent nominal draw factors of 0.2, 0.4,
0.6, ...
Page 180
For the sake of this study the breaking draw ratios from the tensile test were
discounted by the retraction draw ratios to account for the relaxation. The initial
modulus of the drawn sample appears to be the simple combination of the
drawing ...
For the sake of this study the breaking draw ratios from the tensile test were
discounted by the retraction draw ratios to account for the relaxation. The initial
modulus of the drawn sample appears to be the simple combination of the
drawing ...
Page 193
This^m should be used when comparing XRD results with those from other
measurements such as dichroic ratio, NMR, acoustic modulus, and ... The
variation in the orientation and anisotropy indices with draw ratio are plotted in
Figure 5.
This^m should be used when comparing XRD results with those from other
measurements such as dichroic ratio, NMR, acoustic modulus, and ... The
variation in the orientation and anisotropy indices with draw ratio are plotted in
Figure 5.
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Technological Developments in ManMade Fibers and Related | 33 |
Morphology and Near Tm Behavior of High Performance Ultrahigh | 67 |
Properties Structures and Temperature Limitations | 87 |
Copyright | |
22 other sections not shown
Common terms and phrases
1991 John Wiley 3-D braided acrylic fiber alginate fiber amorphous analysis angle Applied Polymer Symposium as-spun axial behavior bending recovery benzyl alcohol birefringence blend break carbon fibers cellulose chain cold drawing compression contact angle cotton fibers crystalline crystallization curve decrease deformation density determined developed diameter distribution DMDHEU draw ratio dye diffusion effect elongation energy experimental fabric failure fiber length fibers spun filament film finish frictional heat treatment impact increase Kevlar liquid m/min material matrix measured mechanical properties modulus molecular molecules nylon obtained orientation parameters PET fibers polyester polyester fibers Polymer Symposium 47 preforms recovery length sample scanning shape parameter shear shown in Figure silicon carbide solvent Spectra composite spinneret spinning speed strain rate stress structure surface Table take-up tenacity tensile tensile strength Text textile thermal treated twist UHMWPE untreated values variability viscosity wettability X-ray diffraction yarn
Bibliographic information
| Title | Science and technology of fibers and related materials: proceedings of the Fiber Society 50th Anniversary Technical Conference held in Princeton, New Jersey, August 19-23, 1990 Volume 47 of Journal of applied polymer science: Applied polymer symposium Volume 47 of Applied polymer symposia |
| Editor | Ludwig Rebenfeld |
| Publisher | Wiley, 1991 |
| Original from | the University of Michigan |
| Digitized | 18 Dec 2007 |
| Length | 534 pages |
| Subjects | Fibers Fibrous composites Polymers Textile fabrics Textile fibers Textile fibers, Synthetic |
| Export Citation | BiBTeX EndNote RefMan |