Page 258
... polyester fibers are thought to be caused by release of stresses in the polyester during solvent swelling . Changes in Dyeing Properties The dyeing properties of untreated and treated polyester samples were ex- amined using four ...
... polyester fibers are thought to be caused by release of stresses in the polyester during solvent swelling . Changes in Dyeing Properties The dyeing properties of untreated and treated polyester samples were ex- amined using four ...
Page 261
... polyester yarns , but in most instances slow the rate of dye adsorption . One of the few exceptions was dyeing of BB - treated polyester with p - nitroaniline where large increases in diffusion coefficients were ... POLYESTER FIBERS 261.
... polyester yarns , but in most instances slow the rate of dye adsorption . One of the few exceptions was dyeing of BB - treated polyester with p - nitroaniline where large increases in diffusion coefficients were ... POLYESTER FIBERS 261.
Page 469
... fiber . The number of cotton and polyester fibers in each annulus was then counted . The experimentally measured fiber diameters for all the fibers were used for calculating fiber volume . RESULTS AND DISCUSSION Fiber Length ...
... fiber . The number of cotton and polyester fibers in each annulus was then counted . The experimentally measured fiber diameters for all the fibers were used for calculating fiber volume . RESULTS AND DISCUSSION Fiber Length ...
Contents
Technological Developments in ManMade Fibers and Related | 33 |
Morphology and Near Tm Behavior of High Performance Ultrahigh | 67 |
Properties Structures and Temperature Limitations | 87 |
Copyright | |
22 other sections not shown
Common terms and phrases
amorphous analysis angle appear Applied assumed behavior bending birefringence blend braided break calculated carpet compared composite compression constant cotton crystalline crystallization curve decrease deformation density dependence described determined developed diameter diffusion direction discussed distance distribution draw effect energy experimental extension fabric factor failure fiber filament finish force fraction function geometry given heat higher impact improved increase indicated initial length liquid load lower m/min material measured mechanical method modulus nylon observed obtained occur orientation parameters phase polyester polymer possible present pressure produced properties range ratio recovery relative sample Scanning shape shear shown in Figure shows solution specimen Spectra speed spinning spun strain strength stress structure surface Table temperature tenacity tensile Text treated treatment twist unit values variability yarn