Microstructure of Cement-Based Systems: Volume 370: Bonding and Interfaces in Cementitious MaterialsThis book continues the MRS series on characteristics and properties of cementitious materials. In Part I, recent advances in microstructure and related characterization of cementitious systems are the focus. Topics include: microstructures of "normal" cement systems; microstructure of 'unusual' cement systems; image analysis, modelling and fractal analysis applications; and assessment of pore structures. Part II features presentations on interfacial microstructures, as well as information on elastic and fracture properties, transport properties, and the effects of interfaces on fiber-reinforced systems. |
From inside the book
Results 1-3 of 9
Page 163
... bricks were the common building materials in Mesopotamia . These bricks were placed on their narrow side . In order to control the plastic and drying shrinkage , sand , rubble , crushed burnt bricks , and straw fibers were added . At ...
... bricks were the common building materials in Mesopotamia . These bricks were placed on their narrow side . In order to control the plastic and drying shrinkage , sand , rubble , crushed burnt bricks , and straw fibers were added . At ...
Page 164
... bricks and mortar ( Figure 2 ) . The latter which is known as khorasan mortar , is typically composed of 60-70 % graded aggregate up to 20 mm in the largest dimension and lime . The aggregate comprises crushed burnt bricks and brick ...
... bricks and mortar ( Figure 2 ) . The latter which is known as khorasan mortar , is typically composed of 60-70 % graded aggregate up to 20 mm in the largest dimension and lime . The aggregate comprises crushed burnt bricks and brick ...
Page 165
... bricks , and sand are embedded in thick layers of carbonated lime . Byzantine Ottoman Figure 2 : A texture of a khorasan mortar . Byzantine and Ottoman masons used equally spaced layers of burnt bricks ( lower ) and mortar ( upper ) for ...
... bricks , and sand are embedded in thick layers of carbonated lime . Byzantine Ottoman Figure 2 : A texture of a khorasan mortar . Byzantine and Ottoman masons used equally spaced layers of burnt bricks ( lower ) and mortar ( upper ) for ...
Contents
APPLICATION OF AUTOMATED IMAGE ANALYSIS TO | 3 |
A REEVALUATION OF HARDENED CEMENT PASTE | 13 |
AN APPROACH TO QUANTITATIVE IMAGE ANALYSIS | 23 |
Copyright | |
47 other sections not shown
Common terms and phrases
1995 Materials Research air voids andesite bond strength bulk cement paste C-S-H gel calcium calcium hydroxide carbonate cement paste cementitious chemical clinker composite compressive strength concentration Concr crack crystals cured curve debonding density diameter dielectric diffusion dynamic modulus effect elastic elastic moduli embedded length energy ettringite experimental fiber reinforced fibres fly ash fracture surface Garboczi grains groundmass hardened hydration products image analysis increase interfacial transition zone interfacial zone load Materials Research Society matrix measured microcracks microscope microstructure mixes modulus mortar observed parameters phase pore size distribution porosity porous portland cement portlandite Proc pullout rock samples sand scanning electron microscope shear shown in Figure shows silica fume solution specimens stress structure sucrose superplasticizer Symp Table tensile thaumasite thickness values volume fraction w/c ratio water-cement ratio wood fiber yarn zeolite