Microstructure of Cement-Based Systems: Volume 370: Bonding and Interfaces in Cementitious MaterialsThis book continues the MRS series on characteristics and properties of cementitious materials. In Part I, recent advances in microstructure and related characterization of cementitious systems are the focus. Topics include: microstructures of "normal" cement systems; microstructure of 'unusual' cement systems; image analysis, modelling and fractal analysis applications; and assessment of pore structures. Part II features presentations on interfacial microstructures, as well as information on elastic and fracture properties, transport properties, and the effects of interfaces on fiber-reinforced systems. |
From inside the book
Results 1-3 of 51
Page 407
... Cement Paste - Aggregate Interfacial Zones in Mortar MENASHI D. COHEN ... cement paste - aggregate interfacial zones in mortar by applying the Logarithmic ... bulk cement paste and interfacial zones of cement paste - aggregate as its ...
... Cement Paste - Aggregate Interfacial Zones in Mortar MENASHI D. COHEN ... cement paste - aggregate interfacial zones in mortar by applying the Logarithmic ... bulk cement paste and interfacial zones of cement paste - aggregate as its ...
Page 424
... PASTE CONSTITUENT The use of silica fume as a cement replacement has been ... bulk cement paste is significantly different from the cement paste within ... Concrete Strength / Mortar Strength 1.1 1 : 3 1 424.
... PASTE CONSTITUENT The use of silica fume as a cement replacement has been ... bulk cement paste is significantly different from the cement paste within ... Concrete Strength / Mortar Strength 1.1 1 : 3 1 424.
Page 435
... cement paste is about 10 times as large as that for the bulk cement paste , in rough agreement with the available mercury intrusion evidence [ 14 ] , and take the interfacial zone conductivity to be about 10 times larger than that of ...
... cement paste is about 10 times as large as that for the bulk cement paste , in rough agreement with the available mercury intrusion evidence [ 14 ] , and take the interfacial zone conductivity to be about 10 times larger than that of ...
Contents
APPLICATION OF AUTOMATED IMAGE ANALYSIS TO | 3 |
A REEVALUATION OF HARDENED CEMENT PASTE | 13 |
AN APPROACH TO QUANTITATIVE IMAGE ANALYSIS | 23 |
Copyright | |
47 other sections not shown
Common terms and phrases
1995 Materials Research air voids andesite bond strength bulk cement paste C-S-H gel calcium calcium hydroxide carbonate cement paste cementitious chemical clinker composite compressive strength concentration Concr crack crystals cured curve debonding density diameter dielectric diffusion dynamic modulus effect elastic elastic moduli embedded length energy ettringite experimental fiber reinforced fibres fly ash fracture surface Garboczi grains groundmass hardened hydration products image analysis increase interfacial transition zone interfacial zone load Materials Research Society matrix measured microcracks microscope microstructure mixes modulus mortar observed parameters phase pore size distribution porosity porous portland cement portlandite Proc pullout rock samples sand scanning electron microscope shear shown in Figure shows silica fume solution specimens stress structure sucrose superplasticizer Symp Table tensile thaumasite thickness values volume fraction w/c ratio water-cement ratio wood fiber yarn zeolite