Microstructure of Cement-Based Systems: Volume 370: Bonding and Interfaces in Cementitious MaterialsThis book continues the MRS series on characteristics and properties of cementitious materials. In Part I, recent advances in microstructure and related characterization of cementitious systems are the focus. Topics include: microstructures of "normal" cement systems; microstructure of 'unusual' cement systems; image analysis, modelling and fractal analysis applications; and assessment of pore structures. Part II features presentations on interfacial microstructures, as well as information on elastic and fracture properties, transport properties, and the effects of interfaces on fiber-reinforced systems. |
From inside the book
Results 1-3 of 81
Page 14
... grains obviously comprise several different types . The brightest features are residual ground cement grains , generally surrounded by thin shells of less bright ( but not visibly porous ) C - S - H hydration product . The entire ...
... grains obviously comprise several different types . The brightest features are residual ground cement grains , generally surrounded by thin shells of less bright ( but not visibly porous ) C - S - H hydration product . The entire ...
Page 125
... grains found in them . A quantitative image analysis was carried out to characterize the shape of the grains of these two ashes from different geographical origins . The main result proves that the higher the glassy particle content of ...
... grains found in them . A quantitative image analysis was carried out to characterize the shape of the grains of these two ashes from different geographical origins . The main result proves that the higher the glassy particle content of ...
Page 133
... grain . Nevertheless this method acknowledges certain limits : the smaller the grain is , the harder the grain extraction becomes . Because surface forces are important at this size , it is difficult to separate physically the sets of ...
... grain . Nevertheless this method acknowledges certain limits : the smaller the grain is , the harder the grain extraction becomes . Because surface forces are important at this size , it is difficult to separate physically the sets of ...
Contents
APPLICATION OF AUTOMATED IMAGE ANALYSIS TO | 3 |
A REEVALUATION OF HARDENED CEMENT PASTE | 13 |
AN APPROACH TO QUANTITATIVE IMAGE ANALYSIS | 23 |
Copyright | |
47 other sections not shown
Common terms and phrases
1995 Materials Research air voids andesite bond strength bulk cement paste C-S-H gel calcium calcium hydroxide carbonate cement paste cementitious chemical clinker composite compressive strength concentration Concr crack crystals cured curve debonding density diameter dielectric diffusion dynamic modulus effect elastic elastic moduli embedded length energy ettringite experimental fiber reinforced fibres fly ash fracture surface Garboczi grains groundmass hardened hydration products image analysis increase interfacial transition zone interfacial zone load Materials Research Society matrix measured microcracks microscope microstructure mixes modulus mortar observed parameters phase pore size distribution porosity porous portland cement portlandite Proc pullout rock samples sand scanning electron microscope shear shown in Figure shows silica fume solution specimens stress structure sucrose superplasticizer Symp Table tensile thaumasite thickness values volume fraction w/c ratio water-cement ratio wood fiber yarn zeolite