Microstructure of Cement-Based Systems: Volume 370: Bonding and Interfaces in Cementitious MaterialsThis book continues the MRS series on characteristics and properties of cementitious materials. In Part I, recent advances in microstructure and related characterization of cementitious systems are the focus. Topics include: microstructures of "normal" cement systems; microstructure of 'unusual' cement systems; image analysis, modelling and fractal analysis applications; and assessment of pore structures. Part II features presentations on interfacial microstructures, as well as information on elastic and fracture properties, transport properties, and the effects of interfaces on fiber-reinforced systems. |
From inside the book
Results 1-3 of 11
Page 24
... the middle of the paste cylinders . These slices were dried using acetone replacement , followed by vacuum drying , and finally by overnight oven drying . The dried slices were impregnated with ultralow viscosity epoxy resin. 24.
... the middle of the paste cylinders . These slices were dried using acetone replacement , followed by vacuum drying , and finally by overnight oven drying . The dried slices were impregnated with ultralow viscosity epoxy resin. 24.
Page 25
... viscosity epoxy resin under vacuum , and polished with diamond paste of progressively finer particle size , spread over Texmet polishing cloth . The finest diamond particle size used was 1 μm . IMAGE ANALYSIS PROCEDURES The SEM image ...
... viscosity epoxy resin under vacuum , and polished with diamond paste of progressively finer particle size , spread over Texmet polishing cloth . The finest diamond particle size used was 1 μm . IMAGE ANALYSIS PROCEDURES The SEM image ...
Page 154
... viscosity using 500 m2 / kg clinker , with varying concentrations of ligninsulphonate + Na2CO3 is represented in Fig . 1 . 1.4- Viscosity ( Pas ) 20 GF cement 550m2 / kg 1 % Na2CO3 + 1.6 -0.8 % LS PC 550 m2 / kg Ligninsulphonate ( wt ...
... viscosity using 500 m2 / kg clinker , with varying concentrations of ligninsulphonate + Na2CO3 is represented in Fig . 1 . 1.4- Viscosity ( Pas ) 20 GF cement 550m2 / kg 1 % Na2CO3 + 1.6 -0.8 % LS PC 550 m2 / kg Ligninsulphonate ( wt ...
Contents
APPLICATION OF AUTOMATED IMAGE ANALYSIS TO | 3 |
A REEVALUATION OF HARDENED CEMENT PASTE | 13 |
AN APPROACH TO QUANTITATIVE IMAGE ANALYSIS | 23 |
Copyright | |
47 other sections not shown
Common terms and phrases
1995 Materials Research air voids andesite bond strength bulk cement paste C-S-H gel calcium calcium hydroxide carbonate cement paste cementitious chemical clinker composite compressive strength concentration Concr crack crystals cured curve debonding density diameter dielectric diffusion dynamic modulus effect elastic elastic moduli embedded length energy ettringite experimental fiber reinforced fibres fly ash fracture surface Garboczi grains groundmass hardened hydration products image analysis increase interfacial transition zone interfacial zone load Materials Research Society matrix measured microcracks microscope microstructure mixes modulus mortar observed parameters phase pore size distribution porosity porous portland cement portlandite Proc pullout rock samples sand scanning electron microscope shear shown in Figure shows silica fume solution specimens stress structure sucrose superplasticizer Symp Table tensile thaumasite thickness values volume fraction w/c ratio water-cement ratio wood fiber yarn zeolite