Neutron Scattering for Materials Science: Volume 166S. M. Shapiro, S. C. Moss, J. D. Jorgensen The MRS Symposium Proceeding series is an internationally recognised reference suitable for researchers and practitioners. |
From inside the book
Results 1-3 of 11
Page 403
... Vycor can be satisfactorily interpreted using a simplified late stage spinodal decomposition model , due to Cahn ' , if one allows for a distribution of wave numbers in the material's density function . The result confirms that the ...
... Vycor can be satisfactorily interpreted using a simplified late stage spinodal decomposition model , due to Cahn ' , if one allows for a distribution of wave numbers in the material's density function . The result confirms that the ...
Page 404
... Vycor was either immersed in the solution to be measured or stored in a dry nitrogen atmosphere . The Vycor samples were all rectangular in shape and were 1.6 mm thick with faces about 5x20 mm . The measurements were performed at the ...
... Vycor was either immersed in the solution to be measured or stored in a dry nitrogen atmosphere . The Vycor samples were all rectangular in shape and were 1.6 mm thick with faces about 5x20 mm . The measurements were performed at the ...
Page 428
... Vycor with a critical fluid mixture imbibed into it , a first striking observation is that the fluid does not phase - separate macroscopically as it does in bulk . The sample develops a uniform cloudiness , which might be due to micro ...
... Vycor with a critical fluid mixture imbibed into it , a first striking observation is that the fluid does not phase - separate macroscopically as it does in bulk . The sample develops a uniform cloudiness , which might be due to micro ...
Contents
THE KINDER GENTLER PROBE OF CONDENSED MATTER | 3 |
NEUTRON SCATTERING METHODS FOR MATERIAL SCIENCE | 15 |
THE ADVANCED NEUTRON SOURCE | 27 |
Copyright | |
65 other sections not shown
Other editions - View all
Common terms and phrases
1990 Materials Research aerogel alloys analysis annealing Argonne National Laboratory atoms beam boron Bragg Bragg peaks calculated composition concentration copolymer correlation decrease density detector determined deuterium diffractometer diffuse scattering displacements distribution effect elastic electronic energy experimental Fermi surface ferroelastic Figure film function incoherent scattering inelastic interface ISBN lattice parameter layers Lett magnetic Materials Research Society measured Metall method mode molecular multilayers National Laboratory neutron diffraction neutron reflectivity neutron scattering Neutron Source observed obtained oxygen oxygen content p-nitroaniline pair interactions particles peak phase phonon Phys plane polymer pore position powder diffraction Proc range reactor residual stresses resolution sample scattering intensity scattering length short-range order shown in Fig shows silica silicon single crystal sintering small angle solid specimen spectrometer stoichiometry strain structure factor superconductivity Symp technique temperature thermal time-of-flight transition tube values vector Vycor wafer wavelength X-ray YBCO