Neutron Scattering for Materials Science: Volume 166S. M. Shapiro, S. C. Moss, J. D. Jorgensen The MRS Symposium Proceeding series is an internationally recognised reference suitable for researchers and practitioners. |
From inside the book
Results 1-3 of 6
Page 195
... YBCO and possibly help reduce the " weak - link " effect [ 5 ] . Note that whereas the addition of a low - volume fraction of silver does not adversely affect the superconductivity the introduction of transition metals to YBCO can have ...
... YBCO and possibly help reduce the " weak - link " effect [ 5 ] . Note that whereas the addition of a low - volume fraction of silver does not adversely affect the superconductivity the introduction of transition metals to YBCO can have ...
Page 196
... YBCO and Ag powders , with 0 , 15 , 20 , and 30 % Ag by volume [ 8 ] . The phase composition of YBCO powder was confirmed by X - ray analysis . The Ag powder had a particle size range of 2-3.5 μm , as indicated by the supplier . Both YBCO ...
... YBCO and Ag powders , with 0 , 15 , 20 , and 30 % Ag by volume [ 8 ] . The phase composition of YBCO powder was confirmed by X - ray analysis . The Ag powder had a particle size range of 2-3.5 μm , as indicated by the supplier . Both YBCO ...
Page 198
... YBCO are known as a function of stoichiometry , it is possible to estimate the diffraction peak shift resulting from strain ( for some diffraction lines ) by correcting for stoichiometry . For example , since the ( 111 ) diffraction ...
... YBCO are known as a function of stoichiometry , it is possible to estimate the diffraction peak shift resulting from strain ( for some diffraction lines ) by correcting for stoichiometry . For example , since the ( 111 ) diffraction ...
Contents
THE KINDER GENTLER PROBE OF CONDENSED MATTER | 3 |
NEUTRON SCATTERING METHODS FOR MATERIAL SCIENCE | 15 |
THE ADVANCED NEUTRON SOURCE | 27 |
Copyright | |
64 other sections not shown
Other editions - View all
Common terms and phrases
1990 Materials Research aerogel alloys analysis angle neutron scattering annealing Argonne Argonne National Laboratory atoms beam boron Bragg Bragg peaks calculated composition concentration copolymer correlation Cu-O decrease defects detector determined deuterated deuterium diffractometer diffuse scattering displacements distribution effect elastic electronic energy experimental Fermi surface ferroelastic Figure film function incoherent scattering increase inelastic interactions interface ISBN lattice parameter layers Lett magnetic Materials Research Society Materials Science measured metals method mode molecular multilayers National Laboratory neutron diffraction neutron powder diffraction neutron reflectivity Neutron Source observed obtained oxygen oxygen content particles peak phase transition phonon Phys plane polymer pore powder diffraction Proc range reactor refinement residual stresses resolution sample scattering intensity short-range order shown in Fig shows silica silicon single crystal sintering specimen spectrometer stoichiometry strain structure factor superconductivity surface Symp technique temperature thermal values Volume Vycor wafer wavelength width X-ray YBCO