John L. Vossen, Werner Kern. observed deposition rate , in the absence of a magnetic field , was a strong function of the source - to - substrate distance ( tripling the distance reduced the rate by 66 % ) . The deposition rate increased ...
John L. Vossen, Werner Kern. observed deposition rate , in the absence of a magnetic field , was a strong function of the source - to - substrate distance ( tripling the distance reduced the rate by 66 % ) . The deposition rate increased ...
Page 343
John L. Vossen, Werner Kern. LPCVD reactors . Deposition rates of 1.2 μm / min have been reported ( 5 sccm WF6 , 6 ... rate occurs at 300 ° C [ 479 ] . Other workers have reported a linear increase of the film deposition rate with in ...
John L. Vossen, Werner Kern. LPCVD reactors . Deposition rates of 1.2 μm / min have been reported ( 5 sccm WF6 , 6 ... rate occurs at 300 ° C [ 479 ] . Other workers have reported a linear increase of the film deposition rate with in ...
Page 493
... rate of 2.4 sccm , for example , the SiO2 deposition rate rose linearly from ~ 140 Å - min1 to almost 600 Å - min ̄ when ~ 3.5 sccm of Si2F6 was introduced to the gas stream . Similar im- provements in deposition rate ( factors of two ...
... rate of 2.4 sccm , for example , the SiO2 deposition rate rose linearly from ~ 140 Å - min1 to almost 600 Å - min ̄ when ~ 3.5 sccm of Si2F6 was introduced to the gas stream . Similar im- provements in deposition rate ( factors of two ...
Contents
Processing Plasmas | 16 |
rf Diode Plasmas | 24 |
Afterglow Plasmas | 37 |
Copyright | |
34 other sections not shown
Other editions - View all
Common terms and phrases
alloy anode Appl applications AsH3 atoms chamber chemical chemical vapor deposition coatings composition compound Crystal Growth density deposition process deposition rate device dielectric dopant doping effects Electrochem emission epitaxial etch rate evaporation excitation film deposition flow flux GaAs gas-phase gases glow discharge grid growth rate heater heating increase ion beam ion bombardment ion energy ion source ionization kinetic laser layer Lett LPCVD magnetic field magnetron material metal molecules nitride OMVPE optical oxide particle PECVD photochemical photodeposition photon photoresist Phys plasma plasma etching potential precursor pressure Proc produce pump ratio reactants reaction reactor region remote PECVD semiconductor shown in Fig SiH4 silane silicon silicon nitride SiO2 sol-gel species sputter deposition sputtering stoichiometric substrate substrate temperature surface susceptor target techniques Technol Technology thermal thickness thin film Thin Solid Films tion torr typically vacuum voltage wafer wavelength