Page 350
... precursor ( Me3N ) 2AlH3 for hot - wall LPCVD at 180 ° C substrate temperature and 25 ° C precursor temperature without carrier gas , the deposition rate was 0.9 μm / min ; at 280 ° C , it was 3 μm / min . The Al films had a rough ...
... precursor ( Me3N ) 2AlH3 for hot - wall LPCVD at 180 ° C substrate temperature and 25 ° C precursor temperature without carrier gas , the deposition rate was 0.9 μm / min ; at 280 ° C , it was 3 μm / min . The Al films had a rough ...
Page 377
... precursor development , in particular in the development of alternative precursors to the highly toxic group V and VI hydrides - e.g . , AsH3 , PH3 , and H2Se . A number of reviews of precursor selection and reactions have appeared ...
... precursor development , in particular in the development of alternative precursors to the highly toxic group V and VI hydrides - e.g . , AsH3 , PH3 , and H2Se . A number of reviews of precursor selection and reactions have appeared ...
Page 475
... precursor for optical source wavelengths below 200 nm . Considerably less is known of the photodeposition of Ga and ... precursor , and broad - area deposition rates up to 1,700 Å - min1 obtained at 248 nm [ 49 ] . If one resorts to WF6 ...
... precursor for optical source wavelengths below 200 nm . Considerably less is known of the photodeposition of Ga and ... precursor , and broad - area deposition rates up to 1,700 Å - min1 obtained at 248 nm [ 49 ] . If one resorts to WF6 ...
Other editions - View all
Common terms and phrases
alloy anode Appl applications AsH3 atoms cathode chamber chemical chemical vapor deposition coatings composition compound semiconductors compounds Crystal Growth CVD reactors density deposition process deposition rate device dielectric diffusion dopant doping effects Electrochem electron emission epitaxial etch rate film deposition flux GaAs gas-phase gases glow discharge grid growth rate heating increase ion beam ion bombardment ion energy ion source ionization K. F. Jensen kinetics laser layer Lett LPCVD magnetic field magnetron material metal mtorr nitride nucleation OMVPE optical oxide particle PECVD photochemical photodeposition photoresist Phys plasma plasma etching potential precursor pressure Proc produce pump ratio reactants reactive region remote PECVD semiconductor SiH4 silane silicides silicon silicon nitride SiO2 sol-gel species sputter deposition sputtering substrate substrate temperature susceptor target techniques Technol Technology thermal thin films Thin Solid Films tion torr typically vacuum voltage wafer wavelength