Thin Film Processes, Volume 1John L. Vossen, Werner Kern Remarkable advances have been made in recent years in the science and technology of thin film processes for deposition and etching. It is the purpose of this book to bring together tutorial reviews of selected filmdeposition and etching processes from a process viewpoint. Emphasis is placed on the practical use of the processes to provide working guidelines for their implementation, a guide to the literature, and an overview of each process. |
From inside the book
Results 1-3 of 81
Page 41
... material ) , or jamming of moving parts ( e.g. , substrate carriers ) . It is especially helpful if sputtering ... material to be deposited , mini- mizing subsequent contamination . A. Target Materials While it is possible to use ...
... material ) , or jamming of moving parts ( e.g. , substrate carriers ) . It is especially helpful if sputtering ... material to be deposited , mini- mizing subsequent contamination . A. Target Materials While it is possible to use ...
Page 43
... material [ 209 ] and render it very difficult to re- move [ 21 ] . In most cases organic contaminants can be removed by chemical sput- tering in O , [ 111 , 112 , 210 ] . Clearly , this will not be adequate if there is continuous ...
... material [ 209 ] and render it very difficult to re- move [ 21 ] . In most cases organic contaminants can be removed by chemical sput- tering in O , [ 111 , 112 , 210 ] . Clearly , this will not be adequate if there is continuous ...
Page 373
... material ( e.g. , ethylene ) could not even initiate a glow discharge with an- other starting material ( e.g. , n - hexane ) under otherwise identical condi- tions . In other words , a relative level of discharge power which varies ac ...
... material ( e.g. , ethylene ) could not even initiate a glow discharge with an- other starting material ( e.g. , n - hexane ) under otherwise identical condi- tions . In other words , a relative level of discharge power which varies ac ...
Contents
Glow Discharge Sputter Deposition | 13 |
Equipment Configuration | 31 |
Preconditioning of Targets Substrates and Systems for Film | 41 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
Å/min alloys anode Appl applications argon atoms bias bombardment cathode Chem chemical coatings composition compounds current density deposition rate dielectric discharge power effect electric Electrochem electron electroplating energy Epitaxial etch rate etchants etching processes film deposition flow rate GaAs gases glow discharge polymerization H₂ H₂O heating HNO3 increase ion beam deposition ion source ionization layer mA/cm² magnetic field magnetron mask metal mTorr N₂ nitride O₂ operation oxide photoresist Phys planar plasma plasma etching plating PM sputtering polishing polymer polymer deposition potential pressure Proc produce ratio reactants reaction reactive sputtering reactor Section semiconductor shown in Fig silicon silicon nitride SiO2 solution species sputter deposition Sputter Gun sputtering yield starting material stoichiometry substrate susceptor target surface techniques Technol temperature thermal thickness Thin Film Thin Solid Films tion U.S. Patent uniform vacuum vapor voltage wafer York µm/min