... carried out . In the T - cross test , GMAW was carried out crossing on a seam weld bead and then hardness measurements were carried out on heat affected seam weld metal by GMAW thermal cycles . GMAW welding parameters are listed in ...
... carried out . In the T - cross test , GMAW was carried out crossing on a seam weld bead and then hardness measurements were carried out on heat affected seam weld metal by GMAW thermal cycles . GMAW welding parameters are listed in ...
Page 135
... carried out using flanges . In late 1990 SSOL were contracted to carry out the tie - in of a 20km carbon steel / 316L ( stainless steel ) clad pipeline in New Zealand for Heeremac V.o.f. These two projects represent significant ...
... carried out using flanges . In late 1990 SSOL were contracted to carry out the tie - in of a 20km carbon steel / 316L ( stainless steel ) clad pipeline in New Zealand for Heeremac V.o.f. These two projects represent significant ...
Page 139
... carried out until the 02 content was less than 500 ppm during the rooting work . Purging took 30 minutes on average . The hyperbaric welding procedures for the duplex pipe material were carried out within an Argon filled tent at a ...
... carried out until the 02 content was less than 500 ppm during the rooting work . Purging took 30 minutes on average . The hyperbaric welding procedures for the duplex pipe material were carried out within an Argon filled tent at a ...
Contents
WELD METAL AND HAZ PROPERTIES | 1 |
ADVANCES IN STEEL AND WELDING | 65 |
Development of HSLA Steel With 80Ksi Yield Strength for Offshore Tubular Applications | 73 |
Copyright | |
22 other sections not shown
Other editions - View all
Common terms and phrases
amplitude analysis applied assessment austenite axial load base metal behaviour bending bolt bolted joint brace brittle calculated CGHAZ chord composite compression crack depth crack front CTOD curve defects delamination diameter duplex effect elastic elastomer energy equations experimental failure fatigue crack growth fatigue tests ferrite finite element flexelement fracture mechanics fracture toughness fume Geesthacht geometry grain heat affected zone heat input HNBR HSLA Steels hydrogen hyperbaric increase interaction laminate layer metal yield strength method microstructure nitrogen notch obtained Offshore Structures OMAE parameters pipe plastic predictions preferential corrosion pressure procedure properties ratio region shear Shielding gas shown in Figure specimens stainless steels strain stress concentration stress intensity factors stress range surface crack T-joint Table temperature tensile strength tension thermal cycle thickness thread tubes tubular joints underwater values weld toe welded joints weldment wire yield strength zone