Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 11, Part 3American Society of Mechanical Engineers, 1992 - Arctic regions |
From inside the book
Results 1-3 of 54
Page 301
... chord thickness . Both values of the applied load , P , and normalised load is given for the whole T - joint , hence , Рo = ( лdt σy ) = 4707 KN . The normalised overall load displacement curves measured at the end of the brace , are ...
... chord thickness . Both values of the applied load , P , and normalised load is given for the whole T - joint , hence , Рo = ( лdt σy ) = 4707 KN . The normalised overall load displacement curves measured at the end of the brace , are ...
Page 325
... chord was chosen to be 5 times its diameter to eliminate the end effects ( UEG , 1985 ) . The length of the branch ( measured from the point at which the centerline of the chord and the branch intersect ) was taken to be half that of the ...
... chord was chosen to be 5 times its diameter to eliminate the end effects ( UEG , 1985 ) . The length of the branch ( measured from the point at which the centerline of the chord and the branch intersect ) was taken to be half that of the ...
Page 588
... chord . The predictions are not so good for the other cases where the stiffeners are not heavy and a significant part of the loads are transferred to the chord through a mechanism similar to that found in unstiffened joints , and the ...
... chord . The predictions are not so good for the other cases where the stiffeners are not heavy and a significant part of the loads are transferred to the chord through a mechanism similar to that found in unstiffened joints , and the ...
Contents
WELD METAL AND HAZ PROPERTIES | 1 |
ADVANCES IN STEEL AND WELDING | 65 |
Development of HSLA Steel With 80Ksi Yield Strength for Offshore Tubular Applications | 73 |
Copyright | |
22 other sections not shown
Other editions - View all
Common terms and phrases
amplitude analysis applied assessment austenite axial load base metal behaviour bending bolt bolted joint brace brittle calculated CGHAZ chord composite compression crack depth crack front CTOD curve defects delamination diameter duplex effect elastic elastomer energy equations experimental failure fatigue crack growth fatigue tests ferrite finite element flexelement fracture mechanics fracture toughness fume Geesthacht geometry grain heat affected zone heat input HNBR HSLA Steels hydrogen hyperbaric increase interaction laminate layer metal yield strength method microstructure nitrogen notch obtained Offshore Structures OMAE parameters pipe plastic predictions preferential corrosion pressure procedure properties ratio region shear Shielding gas shown in Figure specimens stainless steels strain stress concentration stress intensity factors stress range surface crack T-joint Table temperature tensile strength tension thermal cycle thickness thread tubes tubular joints underwater values weld toe welded joints weldment wire yield strength zone