Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 11, Part 3American Society of Mechanical Engineers, 1992 - Arctic regions |
From inside the book
Results 1-3 of 76
Page 95
PREFERENTIAL CORROSION OF WELDMENT OF CARBON STEEL IN CO2 CONTAINING ENVIRONMENT Shigeru Endo , Moriyasu Nagae , and Sakae Fujita Fukuyama Research Department Steel Research Center NKK Corporation Hiroshima , Japan Osamu Hirano Pipe and ...
PREFERENTIAL CORROSION OF WELDMENT OF CARBON STEEL IN CO2 CONTAINING ENVIRONMENT Shigeru Endo , Moriyasu Nagae , and Sakae Fujita Fukuyama Research Department Steel Research Center NKK Corporation Hiroshima , Japan Osamu Hirano Pipe and ...
Page 104
... corrosion appeared initially as rust staining on the surface ; closer examination revealed patches of etched metal surface with small shallow pits . Further evidence of corrosion was visible at the pipe end where a crevice was ...
... corrosion appeared initially as rust staining on the surface ; closer examination revealed patches of etched metal surface with small shallow pits . Further evidence of corrosion was visible at the pipe end where a crevice was ...
Page 597
DISCUSSION Corrosion Behavior in HCl The corrosion resistance of TIMETAL * 21S + Pd was by far superior to any other titanium alloy . The resistance of TIMETAL 21S has been shown to be superior in lower concentrations of hydrochloric ...
DISCUSSION Corrosion Behavior in HCl The corrosion resistance of TIMETAL * 21S + Pd was by far superior to any other titanium alloy . The resistance of TIMETAL 21S has been shown to be superior in lower concentrations of hydrochloric ...
Contents
WELD METAL AND HAZ PROPERTIES | 1 |
ADVANCES IN STEEL AND WELDING | 65 |
Development of HSLA Steel With 80Ksi Yield Strength for Offshore Tubular Applications | 73 |
Copyright | |
22 other sections not shown
Other editions - View all
Common terms and phrases
amplitude analysis applied assessment austenite axial load base metal behaviour bending bolt bolted joint brace brittle calculated CGHAZ chord composite compression crack depth crack front CTOD curve defects delamination diameter duplex effect elastic elastomer energy equations experimental failure fatigue crack growth fatigue tests ferrite finite element flexelement fracture mechanics fracture toughness fume Geesthacht geometry grain heat affected zone heat input HNBR HSLA Steels hydrogen hyperbaric increase interaction laminate layer metal yield strength method microstructure nitrogen notch obtained Offshore Structures OMAE parameters pipe plastic predictions preferential corrosion pressure procedure properties ratio region shear Shielding gas shown in Figure specimens stainless steels strain stress concentration stress intensity factors stress range surface crack T-joint Table temperature tensile strength tension thermal cycle thickness thread tubes tubular joints underwater values weld toe welded joints weldment wire yield strength zone