... hardness and strength in the coarse grained heat affected zone at 1 kJ / mm , the hardness and strength values are 263 HV and 589 MPa , respectively . Hence , safe welding of the other steels require a preheating above room temperature ...
... hardness and strength in the coarse grained heat affected zone at 1 kJ / mm , the hardness and strength values are 263 HV and 589 MPa , respectively . Hence , safe welding of the other steels require a preheating above room temperature ...
Page 131
... hardness traverses of the cut edges . These hardness values in connection with very small applied pressures of load are however considerably higher than those with 5 kp or 10 kp as for example specified the German Industrial Standard ...
... hardness traverses of the cut edges . These hardness values in connection with very small applied pressures of load are however considerably higher than those with 5 kp or 10 kp as for example specified the German Industrial Standard ...
Page 233
... hardness . Hardness , measured in Shore A units , is an indirect measurement of a material's modulus . The hardness measuring device applies a specified load through a truncated cone indentor to the surface of a rubber part . The ...
... hardness . Hardness , measured in Shore A units , is an indirect measurement of a material's modulus . The hardness measuring device applies a specified load through a truncated cone indentor to the surface of a rubber part . The ...
Contents
WELD METAL AND HAZ PROPERTIES | 1 |
ADVANCES IN STEEL AND WELDING | 65 |
Development of HSLA Steel With 80Ksi Yield Strength for Offshore Tubular Applications | 73 |
Copyright | |
22 other sections not shown
Other editions - View all
Common terms and phrases
amplitude analysis applied assessment austenite axial load base metal behaviour bending bolt bolted joint brace brittle calculated CGHAZ chord composite compression crack depth crack front CTOD curve defects delamination diameter duplex effect elastic elastomer energy equations experimental failure fatigue crack growth fatigue tests ferrite finite element flexelement fracture mechanics fracture toughness fume Geesthacht geometry grain heat affected zone heat input HNBR HSLA Steels hydrogen hyperbaric increase interaction laminate layer metal yield strength method microstructure nitrogen notch obtained Offshore Structures OMAE parameters pipe plastic predictions preferential corrosion pressure procedure properties ratio region shear Shielding gas shown in Figure specimens stainless steels strain stress concentration stress intensity factors stress range surface crack T-joint Table temperature tensile strength tension thermal cycle thickness thread tubes tubular joints underwater values weld toe welded joints weldment wire yield strength zone