... materials , to investigate the cause of the problem . In this particular case , the material was able to be used and further delays minimised after a fitness - for - purpose exercise was carried out to confirm that the material had ...
... materials , to investigate the cause of the problem . In this particular case , the material was able to be used and further delays minimised after a fitness - for - purpose exercise was carried out to confirm that the material had ...
Page 496
... material Behaviour during stress - age testing at test temperature specified in Guidance Notes 5 % strain 5 % strain 5 % strain Pretemper 5 % strain only + 1hr + varied strain + 1hr 250 ° C + age Poor ... material , and on 20mm material 496.
... material Behaviour during stress - age testing at test temperature specified in Guidance Notes 5 % strain 5 % strain 5 % strain Pretemper 5 % strain only + 1hr + varied strain + 1hr 250 ° C + age Poor ... material , and on 20mm material 496.
Page 500
... material studied , like many modern steels , exhibits a steep transition curve and SO two materials showing good initial toughness may exhibit completely different strain - age and FL + 5mm behaviour due to their different initial ...
... material studied , like many modern steels , exhibits a steep transition curve and SO two materials showing good initial toughness may exhibit completely different strain - age and FL + 5mm behaviour due to their different initial ...
Contents
WELD METAL AND HAZ PROPERTIES | 1 |
ADVANCES IN STEEL AND WELDING | 65 |
The Corrosion Performance of Materials for Topsides Pipework | 103 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
amplitude analysis applied assessment austenite axial load base metal behaviour bending bolt bolted joint brace brittle calculated CGHAZ chord composite compression crack depth crack front CTOD curve damage defects delamination diameter distribution duplex effect elastic elastomer energy equations experimental failure fatigue crack growth fatigue tests ferrite finite element flexelement fracture mechanics fracture toughness Geesthacht geometry grain heat affected zone heat input HNBR HSLA Steels hydrogen hyperbaric increase initial interaction laminate metal yield strength method microstructure nitrogen notch obtained Offshore Structures OMAE parameters pipe plastic plate predictions preferential corrosion pressure procedure properties ratio region shear Shielding gas shown in Figure simulation specimens stainless steels strain stress concentration stress intensity factors stress range T-joint Table temperature tensile strength tension thermal cycle thickness thread tubes tubular joints underwater values weld toe welded joints weldment yield strength zone