Page 97
... mechanical test . Fracture appearance transition temperature temperature ( vTrs ) measured in Charpy test . Mark ... mechanical properties of girth welded joints using commercial welding consumables Preferential corrosion and mechanical ...
... mechanical test . Fracture appearance transition temperature temperature ( vTrs ) measured in Charpy test . Mark ... mechanical properties of girth welded joints using commercial welding consumables Preferential corrosion and mechanical ...
Page 101
... mechanical properties could be obtained in Mo - containing weld metals . Preferential corrosion and mechanical properties of girth welded joints using commercial welding consumables Mechanical properties and preferential corrosion ...
... mechanical properties could be obtained in Mo - containing weld metals . Preferential corrosion and mechanical properties of girth welded joints using commercial welding consumables Mechanical properties and preferential corrosion ...
Page 249
... Mechanical Engineers , USA The Norwegian Society of Chartered Engineers , Norway Dansk Ingeniorforening , Denmark American Concrete Institute , USA Energy Rubber Group , A.C.S. , USA American Society of Civil Engineers , USA Conseil de ...
... Mechanical Engineers , USA The Norwegian Society of Chartered Engineers , Norway Dansk Ingeniorforening , Denmark American Concrete Institute , USA Energy Rubber Group , A.C.S. , USA American Society of Civil Engineers , USA Conseil de ...
Contents
WELD METAL AND HAZ PROPERTIES | 1 |
ADVANCES IN STEEL AND WELDING | 65 |
The Corrosion Performance of Materials for Topsides Pipework | 103 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
amplitude analysis applied assessment austenite axial load base metal behaviour bending bolt bolted joint brace brittle calculated CGHAZ chord composite compression crack depth crack front CTOD curve damage defects delamination diameter distribution duplex effect elastic elastomer energy equations experimental failure fatigue crack growth fatigue tests ferrite finite element flexelement fracture mechanics fracture toughness Geesthacht geometry grain heat affected zone heat input HNBR HSLA Steels hydrogen hyperbaric increase initial interaction laminate metal yield strength method microstructure nitrogen notch obtained Offshore Structures OMAE parameters pipe plastic plate predictions preferential corrosion pressure procedure properties ratio region shear Shielding gas shown in Figure simulation specimens stainless steels strain stress concentration stress intensity factors stress range T-joint Table temperature tensile strength tension thermal cycle thickness thread tubes tubular joints underwater values weld toe welded joints weldment yield strength zone