Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 11, Part 3American Society of Mechanical Engineers, 1992 - Arctic regions |
From inside the book
Results 1-3 of 69
Page 251
... Mode I , but mixed mode displacements occur when crack growth is initiated under one loading axis and continued under another loading axis . The relevance of previous studies on mixed mode and related fatigue crack growth problems to ...
... Mode I , but mixed mode displacements occur when crack growth is initiated under one loading axis and continued under another loading axis . The relevance of previous studies on mixed mode and related fatigue crack growth problems to ...
Page 252
... Mode I displacements , and during subsequent crack growth , especially when Mode I facets are formed , makes calculation of stress intensity factors difficult ( 2 ) . In the analysis of crack growth data for complex crack paths it is ...
... Mode I displacements , and during subsequent crack growth , especially when Mode I facets are formed , makes calculation of stress intensity factors difficult ( 2 ) . In the analysis of crack growth data for complex crack paths it is ...
Page 255
... Mode I stress intensity factors which would permit the use of Mode I crack growth data . This does not appear to be feasible at the present state - of - the - art . Secondly , the development of laboratory specimens which mimic the ...
... Mode I stress intensity factors which would permit the use of Mode I crack growth data . This does not appear to be feasible at the present state - of - the - art . Secondly , the development of laboratory specimens which mimic the ...
Contents
WELD METAL AND HAZ PROPERTIES | 1 |
ADVANCES IN STEEL AND WELDING | 65 |
The Corrosion Performance of Materials for Topsides Pipework | 103 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
amplitude analysis applied assessment austenite axial load base metal behaviour bending bolt bolted joint brace brittle calculated CGHAZ chord composite compression crack depth crack front CTOD curve damage defects delamination diameter distribution duplex effect elastic elastomer energy equations experimental failure fatigue crack growth fatigue tests ferrite finite element flexelement fracture mechanics fracture toughness Geesthacht geometry grain heat affected zone heat input HNBR HSLA Steels hydrogen hyperbaric increase initial interaction laminate metal yield strength method microstructure nitrogen notch obtained Offshore Structures OMAE parameters pipe plastic plate predictions preferential corrosion pressure procedure properties ratio region shear Shielding gas shown in Figure simulation specimens stainless steels strain stress concentration stress intensity factors stress range T-joint Table temperature tensile strength tension thermal cycle thickness thread tubes tubular joints underwater values weld toe welded joints weldment yield strength zone