Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 11, Part 3American Society of Mechanical Engineers, 1992 - Arctic regions |
From inside the book
Results 1-3 of 87
Page 136
... pipe stainless steel of was it would to an Indexing from therefore adopted but cladding being only 3mm thick skimming the internal bore to match the pipe external circumference could not be carried the stainless steel cladding have ...
... pipe stainless steel of was it would to an Indexing from therefore adopted but cladding being only 3mm thick skimming the internal bore to match the pipe external circumference could not be carried the stainless steel cladding have ...
Page 200
... pipe installation studies was the Heidrun Field in the North Sea . The main conclusions from these studies are : Spooling The pipe can be spooled and stored on a reel , but must be continuously tensioned during the spooling and re ...
... pipe installation studies was the Heidrun Field in the North Sea . The main conclusions from these studies are : Spooling The pipe can be spooled and stored on a reel , but must be continuously tensioned during the spooling and re ...
Page 203
... pipe and the rollers to soften the introduction of load . The spacing between the two lower reaction rollers was 24 - inches and the maximum deflection imposed at the centre of the span was 0.6 - inch . The pipe was repeatedly bent ...
... pipe and the rollers to soften the introduction of load . The spacing between the two lower reaction rollers was 24 - inches and the maximum deflection imposed at the centre of the span was 0.6 - inch . The pipe was repeatedly bent ...
Contents
WELD METAL AND HAZ PROPERTIES | 1 |
ADVANCES IN STEEL AND WELDING | 65 |
Development of HSLA Steel With 80Ksi Yield Strength for Offshore Tubular Applications | 73 |
Copyright | |
22 other sections not shown
Other editions - View all
Common terms and phrases
amplitude analysis applied assessment austenite axial load base metal behaviour bending bolt bolted joint brace brittle calculated CGHAZ chord composite compression crack depth crack front CTOD curve defects delamination diameter duplex effect elastic elastomer energy equations experimental failure fatigue crack growth fatigue tests ferrite finite element flexelement fracture mechanics fracture toughness fume Geesthacht geometry grain heat affected zone heat input HNBR HSLA Steels hydrogen hyperbaric increase interaction laminate layer metal yield strength method microstructure nitrogen notch obtained Offshore Structures OMAE parameters pipe plastic predictions preferential corrosion pressure procedure properties ratio region shear Shielding gas shown in Figure specimens stainless steels strain stress concentration stress intensity factors stress range surface crack T-joint Table temperature tensile strength tension thermal cycle thickness thread tubes tubular joints underwater values weld toe welded joints weldment wire yield strength zone