Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 11, Part 3American Society of Mechanical Engineers, 1992 - Arctic regions |
From inside the book
Results 1-3 of 84
Page 231
... temperatures . Low temperature sealing historically has not been a critical factor in performance of downhole equipment . However , with the advent of some new completion practices low temperature performance is taking on a new ...
... temperatures . Low temperature sealing historically has not been a critical factor in performance of downhole equipment . However , with the advent of some new completion practices low temperature performance is taking on a new ...
Page 232
... temperatures are raised to some level above the crystallization temperature . THERMAL STIFFENING There is a more direct effect of lowering temperatures which cause increased stiffness of a polymer just as soon as thermal equilibrium is ...
... temperatures are raised to some level above the crystallization temperature . THERMAL STIFFENING There is a more direct effect of lowering temperatures which cause increased stiffness of a polymer just as soon as thermal equilibrium is ...
Page 500
... temperature relative to test temperature of -40 ° C . welding , but this may not be detected by testing at a single temperature depending on the magnitude of the shift , and the subsequent position of the transition temperature relative ...
... temperature relative to test temperature of -40 ° C . welding , but this may not be detected by testing at a single temperature depending on the magnitude of the shift , and the subsequent position of the transition temperature relative ...
Contents
WELD METAL AND HAZ PROPERTIES | 1 |
ADVANCES IN STEEL AND WELDING | 65 |
Development of HSLA Steel With 80Ksi Yield Strength for Offshore Tubular Applications | 73 |
Copyright | |
22 other sections not shown
Other editions - View all
Common terms and phrases
amplitude analysis applied assessment austenite axial load base metal behaviour bending bolt bolted joint brace brittle calculated CGHAZ chord composite compression crack depth crack front CTOD curve defects delamination diameter duplex effect elastic elastomer energy equations experimental failure fatigue crack growth fatigue tests ferrite finite element flexelement fracture mechanics fracture toughness fume Geesthacht geometry grain heat affected zone heat input HNBR HSLA Steels hydrogen hyperbaric increase interaction laminate layer metal yield strength method microstructure nitrogen notch obtained Offshore Structures OMAE parameters pipe plastic predictions preferential corrosion pressure procedure properties ratio region shear Shielding gas shown in Figure specimens stainless steels strain stress concentration stress intensity factors stress range surface crack T-joint Table temperature tensile strength tension thermal cycle thickness thread tubes tubular joints underwater values weld toe welded joints weldment wire yield strength zone