Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 11, Part 3American Society of Mechanical Engineers, 1992 - Arctic regions |
From inside the book
Results 1-3 of 83
Page 82
... tensile specimens . FAILURE ANALYSIS Fractographic examination of the failed tensile specimens showed that the longitudinal fracture surface , shown in Figure 2 , is a typical brittle fracture . Microstructure examination of samples ...
... tensile specimens . FAILURE ANALYSIS Fractographic examination of the failed tensile specimens showed that the longitudinal fracture surface , shown in Figure 2 , is a typical brittle fracture . Microstructure examination of samples ...
Page 90
... tensile properties of line pipes steel supplied by six different manufacturers ( YS = 485 MPa ) . Table to API 5LX70 YS supply range ( MPa ) Mill Min . Max . Ave. A 499 547 520 48 B 498 554 524 56 C 492 598 542 106 D 541 631 581 90 E ...
... tensile properties of line pipes steel supplied by six different manufacturers ( YS = 485 MPa ) . Table to API 5LX70 YS supply range ( MPa ) Mill Min . Max . Ave. A 499 547 520 48 B 498 554 524 56 C 492 598 542 106 D 541 631 581 90 E ...
Page 91
... tensile testing . The information obtained from ' standard ' all weld metal tensile test pieces ( manufacturer's quality control test ) is far from ideal ( ' Standard ' test pieces are taken from a sample joint between 1 inch / 25 mm ...
... tensile testing . The information obtained from ' standard ' all weld metal tensile test pieces ( manufacturer's quality control test ) is far from ideal ( ' Standard ' test pieces are taken from a sample joint between 1 inch / 25 mm ...
Contents
WELD METAL AND HAZ PROPERTIES | 1 |
ADVANCES IN STEEL AND WELDING | 65 |
The Corrosion Performance of Materials for Topsides Pipework | 103 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
amplitude analysis applied assessment austenite axial load base metal behaviour bending bolt bolted joint brace brittle calculated CGHAZ chord composite compression crack depth crack front CTOD curve damage defects delamination diameter distribution duplex effect elastic elastomer energy equations experimental failure fatigue crack growth fatigue tests ferrite finite element flexelement fracture mechanics fracture toughness Geesthacht geometry grain heat affected zone heat input HNBR HSLA Steels hydrogen hyperbaric increase initial interaction laminate metal yield strength method microstructure nitrogen notch obtained Offshore Structures OMAE parameters pipe plastic plate predictions preferential corrosion pressure procedure properties ratio region shear Shielding gas shown in Figure simulation specimens stainless steels strain stress concentration stress intensity factors stress range T-joint Table temperature tensile strength tension thermal cycle thickness thread tubes tubular joints underwater values weld toe welded joints weldment yield strength zone