Materials Selection for Process Plants |
From inside the book
Results 1-3 of 57
Page 49
... Elongation % 36 28 Reduction of area % 68 55 Hardness Brinell 130 170 ཋ ༤ སྶཝ་ྒ 110 125 185 84 125 20 12 55 36 240 260 360 1 Hot rolled . gree of cold - working or heat - treatment . As the steel becomes harder and stronger , the elongation ...
... Elongation % 36 28 Reduction of area % 68 55 Hardness Brinell 130 170 ཋ ༤ སྶཝ་ྒ 110 125 185 84 125 20 12 55 36 240 260 360 1 Hot rolled . gree of cold - working or heat - treatment . As the steel becomes harder and stronger , the elongation ...
Page 247
... elongation and hardness are dependent on compounding and blending , and vary from 400-650 per cent elongation and from 40-90 Shore A hardness . Typical properties are tabulated in Table 19.5 . The resilience is good but does not compare ...
... elongation and hardness are dependent on compounding and blending , and vary from 400-650 per cent elongation and from 40-90 Shore A hardness . Typical properties are tabulated in Table 19.5 . The resilience is good but does not compare ...
Page 250
... Elongation Hardness Service temperatures a . Intermittent b . Continuous c . Minimum Specific gravity psi % 700-1250 230-400 Shore A 50-80 ° F 300 ° F 212 ° F -65 1.35 be used at temperatures from -65 up to 300 ° F and is of prime ...
... Elongation Hardness Service temperatures a . Intermittent b . Continuous c . Minimum Specific gravity psi % 700-1250 230-400 Shore A 50-80 ° F 300 ° F 212 ° F -65 1.35 be used at temperatures from -65 up to 300 ° F and is of prime ...
Contents
INTRODUCTION | 1 |
CATHODIC PROTECTION 2280 | 22 |
INHIBITORS | 28 |
Copyright | |
23 other sections not shown
Other editions - View all
Common terms and phrases
abrasion resistance alkalies aluminum aluminum alloys annealed anode applications austenitic austenitic stainless steels base metal brasses brazing bronzes carbide carbon steel cast iron cathodic cause cements cent chemical resistance chloride chromium coat coefficient of thermal cold-working compounds concentrations copper corrosion resistance cracking ductility effect elastomers electrodes elevated temperatures Elongation environments epoxies equipment exposure fabrication filler film furane grades graphite gray iron handled hardened hardness Hastelloy heat heat-treatment Inconel increase inhibitors machining Manganese material maximum mechanical properties metal surface Monel natural rubber Ni-Resist nickel nitric acid normally oxidizing paint phenolics physical and mechanical pipe plastic process industries protection rate of attack readily reducing Reduction of area resin rust salts sea water silicon sodium solutions solvents stainless steels stress structure sulfuric acid tensile strength Tensile strength psi thermal conductivity thermal expansion tion titanium Type welding wrought Yield strength Yield strength psi zinc zirconium