Materials Selection for Process Plants |
From inside the book
Results 1-3 of 40
Page 12
... brass are more susceptible than the single - phase alpha brasses . Dezincification occurs in many corrosive waters and may take place in those which are alkaline as well as those which are acid . Two types of dezincification are ...
... brass are more susceptible than the single - phase alpha brasses . Dezincification occurs in many corrosive waters and may take place in those which are alkaline as well as those which are acid . Two types of dezincification are ...
Page 154
... Brasses The brasses are probably the most useful of all copper alloys . The term brass was originally applied only to binary alloys of copper and zinc , but today this is not always true . Although there are numerous modified brasses ...
... Brasses The brasses are probably the most useful of all copper alloys . The term brass was originally applied only to binary alloys of copper and zinc , but today this is not always true . Although there are numerous modified brasses ...
Page 156
... brasses with a zinc content below 20 per cent have a chemical resistance paralleling that of electrolytic tough - pitch copper , these brasses are relatively unaffected by dezincification and are used at elevated tem- peratures in the ...
... brasses with a zinc content below 20 per cent have a chemical resistance paralleling that of electrolytic tough - pitch copper , these brasses are relatively unaffected by dezincification and are used at elevated tem- peratures in the ...
Contents
INTRODUCTION | 1 |
CATHODIC PROTECTION 2280 | 22 |
INHIBITORS | 28 |
Copyright | |
23 other sections not shown
Other editions - View all
Common terms and phrases
abrasion resistance alkalies aluminum aluminum alloys annealed anode applications austenitic austenitic stainless steels base metal brasses brazing bronzes carbide carbon steel cast iron cathodic cause cements cent chemical resistance chloride chromium coat coefficient of thermal cold-working compounds concentrations copper corrosion resistance cracking ductility effect elastomers electrodes elevated temperatures Elongation environments epoxies equipment exposure fabrication filler film furane grades graphite gray iron handled hardened hardness Hastelloy heat heat-treatment Inconel increase inhibitors machining Manganese material maximum mechanical properties metal surface Monel natural rubber Ni-Resist nickel nitric acid normally oxidizing paint phenolics physical and mechanical pipe plastic process industries protection rate of attack readily reducing Reduction of area resin rust salts sea water silicon sodium solutions solvents stainless steels stress structure sulfuric acid tensile strength Tensile strength psi thermal conductivity thermal expansion tion titanium Type welding wrought Yield strength Yield strength psi zinc zirconium