Materials Selection for Process Plants |
From inside the book
Results 1-3 of 86
Page 48
... Carbon Manganese Phosphorus Sulfur C1020 C1040 0.18-0.23 0.30-0.60 0.040 max 0.050 max 0.37-0.44 0.60-0.90 0.040 max 0.050 max Balance : iron plus 0.20 % silicon . Steel is iron with small quantities of carbon , silicon , manganese ...
... Carbon Manganese Phosphorus Sulfur C1020 C1040 0.18-0.23 0.30-0.60 0.040 max 0.050 max 0.37-0.44 0.60-0.90 0.040 max 0.050 max Balance : iron plus 0.20 % silicon . Steel is iron with small quantities of carbon , silicon , manganese ...
Page 50
... carbon con- tent . The surface edges to be welded should be clean and properly prepared . In gas - welding , a neutral flame and fast travel are normally employed . The filler rod should have a carbon content comparable to that of the ...
... carbon con- tent . The surface edges to be welded should be clean and properly prepared . In gas - welding , a neutral flame and fast travel are normally employed . The filler rod should have a carbon content comparable to that of the ...
Page 54
... carbon and alloy steels are compared in Table 6.3 . Alloy steels are extra strong , extra tough , and more heat and rust resistant . The hot - forming and cold - forming operations for the low alloy steels are identical to those for carbon ...
... carbon and alloy steels are compared in Table 6.3 . Alloy steels are extra strong , extra tough , and more heat and rust resistant . The hot - forming and cold - forming operations for the low alloy steels are identical to those for carbon ...
Contents
INTRODUCTION | 1 |
CATHODIC PROTECTION 2280 | 22 |
INHIBITORS | 28 |
Copyright | |
23 other sections not shown
Other editions - View all
Common terms and phrases
abrasion resistance alkalies aluminum aluminum alloys annealed anode applications austenitic austenitic stainless steels base metal brasses brazing bronzes carbide carbon steel cast iron cathodic cause cements cent chemical resistance chloride chromium coat coefficient of thermal cold-working compounds concentrations copper corrosion resistance cracking ductility effect elastomers electrodes elevated temperatures Elongation environments epoxies equipment exposure fabrication filler film furane grades graphite gray iron handled hardened hardness Hastelloy heat heat-treatment Inconel increase inhibitors machining Manganese material maximum mechanical properties metal surface Monel natural rubber Ni-Resist nickel nitric acid normally oxidizing paint phenolics physical and mechanical pipe plastic process industries protection rate of attack readily reducing Reduction of area resin rust salts sea water silicon sodium solutions solvents stainless steels stress structure sulfuric acid tensile strength Tensile strength psi thermal conductivity thermal expansion tion titanium Type welding wrought Yield strength Yield strength psi zinc zirconium