Materials Selection for Process Plants |
From inside the book
Results 1-3 of 86
Page 96
... cause corrosion . These parti- cles are best removed by immersing the surface for one hour in a solution that ... cause severe general attack ; if oxidizing , they cause pitting . In the presence of high ten- sile stresses , the pits may ...
... cause corrosion . These parti- cles are best removed by immersing the surface for one hour in a solution that ... cause severe general attack ; if oxidizing , they cause pitting . In the presence of high ten- sile stresses , the pits may ...
Page 97
... cause rapid increase in corrosion rates . At room temperature , 5–85 per cent sulfuric acid causes accelerated attack . Hydrochloric acid promotes pitting attack on the chromium - nickel aus- tenitic steels and the use of austenitic ...
... cause rapid increase in corrosion rates . At room temperature , 5–85 per cent sulfuric acid causes accelerated attack . Hydrochloric acid promotes pitting attack on the chromium - nickel aus- tenitic steels and the use of austenitic ...
Page 138
... cause attack upon aluminum ; exceptions are concentrated nitric acid ( above 82 weight per cent ) and sulfuric acid ... cause severe localized attack of aluminum . Also , the simple acids contain- ing a halogen radical are , in general ...
... cause attack upon aluminum ; exceptions are concentrated nitric acid ( above 82 weight per cent ) and sulfuric acid ... cause severe localized attack of aluminum . Also , the simple acids contain- ing a halogen radical are , in general ...
Contents
INTRODUCTION | 1 |
CATHODIC PROTECTION 2280 | 22 |
INHIBITORS | 28 |
Copyright | |
23 other sections not shown
Other editions - View all
Common terms and phrases
abrasion resistance alkalies aluminum aluminum alloys annealed anode applications austenitic austenitic stainless steels base metal brasses brazing bronzes carbide carbon steel cast iron cathodic cause cements cent chemical resistance chloride chromium coat coefficient of thermal cold-working compounds concentrations copper corrosion resistance cracking ductility effect elastomers electrodes elevated temperatures Elongation environments epoxies equipment exposure fabrication filler film furane grades graphite gray iron handled hardened hardness Hastelloy heat heat-treatment Inconel increase inhibitors machining Manganese material maximum mechanical properties metal surface Monel natural rubber Ni-Resist nickel nitric acid normally oxidizing paint phenolics physical and mechanical pipe plastic process industries protection rate of attack readily reducing Reduction of area resin rust salts sea water silicon sodium solutions solvents stainless steels stress structure sulfuric acid tensile strength Tensile strength psi thermal conductivity thermal expansion tion titanium Type welding wrought Yield strength Yield strength psi zinc zirconium