Materials Selection for Process Plants |
From inside the book
Results 1-3 of 78
Page 149
... copper is poor . In the annealed condition , the tensile strength is only 35,000–45,000 psi ; however , this strength can be TABLE 13.1 . AVERAGE PHYSICAL AND MECHANICAL PROPERTIES OF COPPER 149 COPPER AND COPPER ALLOYS Copper.
... copper is poor . In the annealed condition , the tensile strength is only 35,000–45,000 psi ; however , this strength can be TABLE 13.1 . AVERAGE PHYSICAL AND MECHANICAL PROPERTIES OF COPPER 149 COPPER AND COPPER ALLOYS Copper.
Page 151
... copper and the change in volume will form voids in the copper which then becomes brittle and unusable . Hot - forming operations have merit when sharp bends are desired or when other drastic shape changes are ... COPPER AND COPPER ALLOYS 151.
... copper and the change in volume will form voids in the copper which then becomes brittle and unusable . Hot - forming operations have merit when sharp bends are desired or when other drastic shape changes are ... COPPER AND COPPER ALLOYS 151.
Page 152
... copper . Coated aluminum - bronze electrodes produce the soundest metal - arc - welds . Inert - gas - shielded - arc - welding is satisfactory for joining copper parts up to one half in . thick ; silicon - de- oxidized copper electrodes ...
... copper . Coated aluminum - bronze electrodes produce the soundest metal - arc - welds . Inert - gas - shielded - arc - welding is satisfactory for joining copper parts up to one half in . thick ; silicon - de- oxidized copper electrodes ...
Contents
INTRODUCTION | 1 |
CATHODIC PROTECTION 2280 | 22 |
INHIBITORS | 28 |
Copyright | |
23 other sections not shown
Other editions - View all
Common terms and phrases
abrasion resistance alkalies aluminum aluminum alloys annealed anode applications austenitic austenitic stainless steels base metal brasses brazing bronzes carbide carbon steel cast iron cathodic cause cements cent chemical resistance chloride chromium coat coefficient of thermal cold-working compounds concentrations copper corrosion resistance cracking ductility effect elastomers electrodes elevated temperatures Elongation environments epoxies equipment exposure fabrication filler film furane grades graphite gray iron handled hardened hardness Hastelloy heat heat-treatment Inconel increase inhibitors machining Manganese material maximum mechanical properties metal surface Monel natural rubber Ni-Resist nickel nitric acid normally oxidizing paint phenolics physical and mechanical pipe plastic process industries protection rate of attack readily reducing Reduction of area resin rust salts sea water silicon sodium solutions solvents stainless steels stress structure sulfuric acid tensile strength Tensile strength psi thermal conductivity thermal expansion tion titanium Type welding wrought Yield strength Yield strength psi zinc zirconium