... filler metals with melting points in excess of 800 ° F , while soldering covers the use of filler materials below 800 ° F . Com- monly , in brazing and soldering , the joints are made by flowing the filler metal between closely mated ...
... filler metals with melting points in excess of 800 ° F , while soldering covers the use of filler materials below 800 ° F . Com- monly , in brazing and soldering , the joints are made by flowing the filler metal between closely mated ...
Page 152
... filler metal ; however , phosphorus - de- oxidized copper filler metal is sometimes employed for maximum corrosion resistance . Heat - treatment is not customarily performed on copper . The metal does not normally require annealing or ...
... filler metal ; however , phosphorus - de- oxidized copper filler metal is sometimes employed for maximum corrosion resistance . Heat - treatment is not customarily performed on copper . The metal does not normally require annealing or ...
Page 209
... fillers are silica , carbon , and asbestos . A serious drawback to the widespread usage of polyester cements is their high shrinkage fac- tor ; this can be controlled within limits by varying the styrene content or the amount of filler ...
... fillers are silica , carbon , and asbestos . A serious drawback to the widespread usage of polyester cements is their high shrinkage fac- tor ; this can be controlled within limits by varying the styrene content or the amount of filler ...
Contents
INTRODUCTION | 1 |
CATHODIC PROTECTION 2280 | 22 |
INHIBITORS | 28 |
Copyright | |
23 other sections not shown
Other editions - View all
Common terms and phrases
abrasion resistance alkalies aluminum aluminum alloys annealed anode applications austenitic austenitic stainless steels base metal brasses brazing bronzes carbide carbon steel cast iron cathodic cause cements cent chemical resistance chloride chromium coat coefficient of thermal cold-working compounds concentrations copper corrosion resistance cracking ductility effect elastomers electrodes elevated temperatures Elongation environments epoxies equipment exposure fabrication filler film furane grades graphite gray iron handled hardened hardness Hastelloy heat heat-treatment Inconel increase inhibitors machining Manganese material maximum mechanical properties metal surface Monel natural rubber Ni-Resist nickel nitric acid normally oxidizing paint phenolics physical and mechanical pipe plastic process industries protection rate of attack readily reducing Reduction of area resin rust salts sea water silicon sodium solutions solvents stainless steels stress structure sulfuric acid tensile strength Tensile strength psi thermal conductivity thermal expansion tion titanium Type welding wrought Yield strength Yield strength psi zinc zirconium