Materials Selection for Process Plants |
From inside the book
Results 1-3 of 17
Page 209
... Furane mortars are prepared at the place of use . Two parts by weight of powder and one part by weight of liquid resin are mixed to a smooth consistency . The mortar must be troweled and used immediately . To avoid premature setting of ...
... Furane mortars are prepared at the place of use . Two parts by weight of powder and one part by weight of liquid resin are mixed to a smooth consistency . The mortar must be troweled and used immediately . To avoid premature setting of ...
Page 216
... furane plastics possess good alkali resist- ance . They are condensations products of furfural or furfuryl alcohol . When furane resins are reacted with an acid catalyst , a hard infusible thermo- setting plastic is produced . For ...
... furane plastics possess good alkali resist- ance . They are condensations products of furfural or furfuryl alcohol . When furane resins are reacted with an acid catalyst , a hard infusible thermo- setting plastic is produced . For ...
Page 305
... furane , 208 phenolic , 208 polyester , 209 silicate , 206 sulfur , 207 Formulation , paints alkyd , 270 asphalt ... Furane cements chemical resistance , 209 formulation , 208 temperature limitations , 209 Furane plastics abrasion ...
... furane , 208 phenolic , 208 polyester , 209 silicate , 206 sulfur , 207 Formulation , paints alkyd , 270 asphalt ... Furane cements chemical resistance , 209 formulation , 208 temperature limitations , 209 Furane plastics abrasion ...
Contents
INTRODUCTION | 1 |
CATHODIC PROTECTION 2280 | 22 |
INHIBITORS | 28 |
Copyright | |
23 other sections not shown
Other editions - View all
Common terms and phrases
abrasion resistance alkalies aluminum aluminum alloys annealed anode applications austenitic austenitic stainless steels base metal brasses brazing bronzes carbide carbon steel cast iron cathodic cause cements cent chemical resistance chloride chromium coat coefficient of thermal cold-working compounds concentrations copper corrosion resistance cracking ductility effect elastomers electrodes elevated temperatures Elongation environments epoxies equipment exposure fabrication filler film furane grades graphite gray iron handled hardened hardness Hastelloy heat heat-treatment Inconel increase inhibitors machining Manganese material maximum mechanical properties metal surface Monel natural rubber Ni-Resist nickel nitric acid normally oxidizing paint phenolics physical and mechanical pipe plastic process industries protection rate of attack readily reducing Reduction of area resin rust salts sea water silicon sodium solutions solvents stainless steels stress structure sulfuric acid tensile strength Tensile strength psi thermal conductivity thermal expansion tion titanium Type welding wrought Yield strength Yield strength psi zinc zirconium