Materials Selection for Process Plants |
From inside the book
Results 1-3 of 44
Page 122
... perform the shaping operations . Since " Hastelloy B " work - hardens to a larger extent than the austenitic stainless steels , cold - forming is performed in steps . After each step , the metal part should be annealed to restore the ...
... perform the shaping operations . Since " Hastelloy B " work - hardens to a larger extent than the austenitic stainless steels , cold - forming is performed in steps . After each step , the metal part should be annealed to restore the ...
Page 127
... performed im- mediately after the metal is removed from the furnace . The wrought alloy exhibits good ductility and is amenable to ordinary cold - working operations ; in fact , the equipment used for the stainless steels can be readily ...
... performed im- mediately after the metal is removed from the furnace . The wrought alloy exhibits good ductility and is amenable to ordinary cold - working operations ; in fact , the equipment used for the stainless steels can be readily ...
Page 197
... performed at slow speeds . The metal adheres to the grinding wheel ; special fine soft wheels overcome this tendency . Fine zirconium dust and powder are pyrophoric and may ignite spontaneously ; fine turnings are readily ignited and ...
... performed at slow speeds . The metal adheres to the grinding wheel ; special fine soft wheels overcome this tendency . Fine zirconium dust and powder are pyrophoric and may ignite spontaneously ; fine turnings are readily ignited and ...
Contents
INTRODUCTION | 1 |
CATHODIC PROTECTION 2280 | 22 |
INHIBITORS | 28 |
Copyright | |
23 other sections not shown
Other editions - View all
Common terms and phrases
abrasion resistance alkalies aluminum aluminum alloys annealed anode applications austenitic austenitic stainless steels base metal brasses brazing bronzes carbide carbon steel cast iron cathodic cause cements cent chemical resistance chloride chromium coat coefficient of thermal cold-working compounds concentrations copper corrosion resistance cracking ductility effect elastomers electrodes elevated temperatures Elongation environments epoxies equipment exposure fabrication filler film furane grades graphite gray iron handled hardened hardness Hastelloy heat heat-treatment Inconel increase inhibitors machining Manganese material maximum mechanical properties metal surface Monel natural rubber Ni-Resist nickel nitric acid normally oxidizing paint phenolics physical and mechanical pipe plastic process industries protection rate of attack readily reducing Reduction of area resin rust salts sea water silicon sodium solutions solvents stainless steels stress structure sulfuric acid tensile strength Tensile strength psi thermal conductivity thermal expansion tion titanium Type welding wrought Yield strength Yield strength psi zinc zirconium