... pipe in soil . For well - coated pipe , the cur- rent densities are about 1 per cent of those needed for bare pipe . As the coating deteriorates , the current demand increases and approaches that of bare pipe . The next step is to ...
... pipe in soil . For well - coated pipe , the cur- rent densities are about 1 per cent of those needed for bare pipe . As the coating deteriorates , the current demand increases and approaches that of bare pipe . The next step is to ...
Page 45
... pipe ends . Because standard and 4D wrought iron are red short in the temperature range of 1450-1750 ° F , they are forged at 2400 ° F and other hot - forming operations are performed at 1300 ° F . Man- ganese wrought iron is not red ...
... pipe ends . Because standard and 4D wrought iron are red short in the temperature range of 1450-1750 ° F , they are forged at 2400 ° F and other hot - forming operations are performed at 1300 ° F . Man- ganese wrought iron is not red ...
Page 233
... pipe equipment . Saran pipe by itself is weak and needs either many points of support or contin- uous support ; saran - lined steel requires the same number of hangers as does steel pipe of the same loading . Fluorocarbon Plastics ...
... pipe equipment . Saran pipe by itself is weak and needs either many points of support or contin- uous support ; saran - lined steel requires the same number of hangers as does steel pipe of the same loading . Fluorocarbon Plastics ...
Contents
INTRODUCTION | 1 |
CATHODIC PROTECTION 2280 | 22 |
INHIBITORS | 28 |
Copyright | |
23 other sections not shown
Other editions - View all
Common terms and phrases
abrasion resistance alkalies aluminum aluminum alloys annealed anode applications austenitic austenitic stainless steels base metal brasses brazing bronzes carbide carbon steel cast iron cathodic cause cements cent chemical resistance chloride chromium coat coefficient of thermal cold-working compounds concentrations copper corrosion resistance cracking ductility effect elastomers electrodes elevated temperatures Elongation environments epoxies equipment exposure fabrication filler film furane grades graphite gray iron handled hardened hardness Hastelloy heat heat-treatment Inconel increase inhibitors machining Manganese material maximum mechanical properties metal surface Monel natural rubber Ni-Resist nickel nitric acid normally oxidizing paint phenolics physical and mechanical pipe plastic process industries protection rate of attack readily reducing Reduction of area resin rust salts sea water silicon sodium solutions solvents stainless steels stress structure sulfuric acid tensile strength Tensile strength psi thermal conductivity thermal expansion tion titanium Type welding wrought Yield strength Yield strength psi zinc zirconium