... Pitting Corrosion Pitting is probably the most destructive and unpredictable form of cor- rosion . Normally , only a small amount of metal is lost from the surface , but perforation is often complete . Pitting is difficult to evaluate ...
... Pitting Corrosion Pitting is probably the most destructive and unpredictable form of cor- rosion . Normally , only a small amount of metal is lost from the surface , but perforation is often complete . Pitting is difficult to evaluate ...
Page 97
... pitting and stress - cracking may occur on the underlying metal . All austenitic stainless steels have excellent resistance to nitric acid in all concentrations and at all temperatures . Most nitric acid plants are fabricated from Type ...
... pitting and stress - cracking may occur on the underlying metal . All austenitic stainless steels have excellent resistance to nitric acid in all concentrations and at all temperatures . Most nitric acid plants are fabricated from Type ...
Page 298
... pitting , 109 properties , 108 , 113 uses , 110 , 114 welding , 109 , 114 Alloys aluminum , 138 copper , 154 lead , 186 nickel , 171 , 175 , 177 titanium , 193 zirconium , 200 Aluminum alloys , 138 anodes , 24 properties , 132 soldering ...
... pitting , 109 properties , 108 , 113 uses , 110 , 114 welding , 109 , 114 Alloys aluminum , 138 copper , 154 lead , 186 nickel , 171 , 175 , 177 titanium , 193 zirconium , 200 Aluminum alloys , 138 anodes , 24 properties , 132 soldering ...
Contents
INTRODUCTION | 1 |
CATHODIC PROTECTION 2280 | 22 |
INHIBITORS | 28 |
Copyright | |
23 other sections not shown
Other editions - View all
Common terms and phrases
abrasion resistance alkalies aluminum aluminum alloys annealed anode applications austenitic austenitic stainless steels base metal brasses brazing bronzes carbide carbon steel cast iron cathodic cause cements cent chemical resistance chloride chromium coat coefficient of thermal cold-working compounds concentrations copper corrosion resistance cracking ductility effect elastomers electrodes elevated temperatures Elongation environments epoxies equipment exposure fabrication filler film furane grades graphite gray iron handled hardened hardness Hastelloy heat heat-treatment Inconel increase inhibitors machining Manganese material maximum mechanical properties metal surface Monel natural rubber Ni-Resist nickel nitric acid normally oxidizing paint phenolics physical and mechanical pipe plastic process industries protection rate of attack readily reducing Reduction of area resin rust salts sea water silicon sodium solutions solvents stainless steels stress structure sulfuric acid tensile strength Tensile strength psi thermal conductivity thermal expansion tion titanium Type welding wrought Yield strength Yield strength psi zinc zirconium