Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 13, Parts 3-5American Society of Mechanical Engineers, 1994 - Arctic regions |
From inside the book
Results 1-3 of 34
Page 296
... oxygen and 0.07 wt.pct . carbon as an example , carbon will react with oxygen following path A ( in Figure 7 ) until the equilibrium concentrations of both elements are reached ( 0.02 and 0.07 , respectively ) . The line representing ...
... oxygen and 0.07 wt.pct . carbon as an example , carbon will react with oxygen following path A ( in Figure 7 ) until the equilibrium concentrations of both elements are reached ( 0.02 and 0.07 , respectively ) . The line representing ...
Page 297
... oxygen content . Even though high oxygen content is advantageous to hydrogen control , intentional additions to increase the weld metal oxygen must be limited because of its potentially deteriorating effect on toughness at excessive ...
... oxygen content . Even though high oxygen content is advantageous to hydrogen control , intentional additions to increase the weld metal oxygen must be limited because of its potentially deteriorating effect on toughness at excessive ...
Page 364
... oxygen . The de- oxidants present in the wire and base metal were not sufficient to keep the oxygen content at the initial levels . However the weld metal oxygen content did not increase continuously with the increase of hema- tite ...
... oxygen . The de- oxidants present in the wire and base metal were not sufficient to keep the oxygen content at the initial levels . However the weld metal oxygen content did not increase continuously with the increase of hema- tite ...
Contents
FATIGUE AND DEFORMATION | 1 |
FRACTURE ASSESSMENT AND ANALYSIS | 37 |
FATIGUE DESIGN AND DETECTION | 73 |
Copyright | |
45 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied Arctic Engineering as-welded ASME assessment axial bending cathodic protection Charpy cold deformation corrosion crack growth rate crack propagation crack tip CTOD cycles depth diameter displacement drillpipe elastic electrode equation experimental factor failure fatigue crack growth fatigue strength ferrite finite element fracture mechanics fracture toughness geometry hoop stress hydrogen Ice Class increase load material maximum mbar Mechanics and Arctic method microstructure modulus nitrogen notch obtained Offshore Mechanics offshore structures OMAE operating oxygen parameters pipe pipeline plastic predicted pressure properties ratio region residual stress S-N curve scour sea ice sea water shear shielding gas simulated soil sour crude oil specimens strain rate stress intensity stress range stress relieved surface Table temperature tensile TMCP tubular joints values wall thickness water hammer weld deposit weld metal weld toe welded joints wire yield strength Young's modulus