Page 122
... specimens as well as in tubular joints without the loss of fatigue strength [ Tubby , 1989 , Gibstein et al , 1987 ] . If hammer peening is applied to ground joints , deeper cracks could successfully be removed . When such repairs are ...
... specimens as well as in tubular joints without the loss of fatigue strength [ Tubby , 1989 , Gibstein et al , 1987 ] . If hammer peening is applied to ground joints , deeper cracks could successfully be removed . When such repairs are ...
Page 123
... specimens ) . The mean line for the Class F curve , adjusted to 30 mm thickness according to the DEn 4 thickness correction rule ( DEn , 1984 ) is plotted in the diagrams for comparison . Each of the test series comprised 5 to 11 specimens ...
... specimens ) . The mean line for the Class F curve , adjusted to 30 mm thickness according to the DEn 4 thickness correction rule ( DEn , 1984 ) is plotted in the diagrams for comparison . Each of the test series comprised 5 to 11 specimens ...
Page 422
... specimens were T - joints with fillet welds joining the attachment to the horizontal plate as shown in Figure 2. Specimen dimensions are also shown in Figure 2 . Specimen fabrication . The attachment was welded manually to a 2.5 m long ...
... specimens were T - joints with fillet welds joining the attachment to the horizontal plate as shown in Figure 2. Specimen dimensions are also shown in Figure 2 . Specimen fabrication . The attachment was welded manually to a 2.5 m long ...
Contents
FATIGUE AND DEFORMATION | 1 |
FRACTURE ASSESSMENT AND ANALYSIS | 37 |
FATIGUE DESIGN AND DETECTION | 73 |
Copyright | |
45 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied Arctic Engineering as-welded ASME assessment axial bending cathodic protection Charpy cold deformation corrosion crack growth rate crack propagation crack tip CTOD cycles depth diameter displacement drillpipe elastic electrode equation experimental factor failure fatigue crack growth fatigue strength ferrite finite element fracture mechanics fracture toughness geometry hoop stress hydrogen Ice Class increase load material maximum mbar Mechanics and Arctic method microstructure modulus nitrogen notch obtained Offshore Mechanics offshore structures OMAE operating oxygen parameters pipe pipeline plastic predicted pressure properties ratio region residual stress S-N curve scour sea ice sea water shear shielding gas simulated soil sour crude oil specimens strain rate stress intensity stress range stress relieved surface Table temperature tensile TMCP tubular joints values wall thickness water hammer weld deposit weld metal weld toe welded joints wire yield strength Young's modulus