Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 13, Parts 3-5American Society of Mechanical Engineers, 1994 - Arctic regions |
From inside the book
Results 1-3 of 23
Page 316
... stress relieved conditions . The specimens are necked in an elliptical shape which indicates the anisotropic nature of the steel . The specimens tested in the stress relieved condition , the center line delaminations were observed for ...
... stress relieved conditions . The specimens are necked in an elliptical shape which indicates the anisotropic nature of the steel . The specimens tested in the stress relieved condition , the center line delaminations were observed for ...
Page 318
... stress relieved ( SR ) conditions in rolling direction ( RD ) and transverse ( T ) orientations . All specimens showed a ductile mode of failure at at -20 ° C test temperature and hence toughness values refer to the maximum load ( 8m ) ...
... stress relieved ( SR ) conditions in rolling direction ( RD ) and transverse ( T ) orientations . All specimens showed a ductile mode of failure at at -20 ° C test temperature and hence toughness values refer to the maximum load ( 8m ) ...
Page 21
... relieved condition before welding , would a second stress relieving operation after welding have a further detrimental effect on the mechanical properties ? Two cases were studied ... STRESS RELIEVING OPERATION ON TENSILE TESTS ASME 21.
... relieved condition before welding , would a second stress relieving operation after welding have a further detrimental effect on the mechanical properties ? Two cases were studied ... STRESS RELIEVING OPERATION ON TENSILE TESTS ASME 21.
Contents
FATIGUE AND DEFORMATION | 1 |
FRACTURE ASSESSMENT AND ANALYSIS | 37 |
FATIGUE DESIGN AND DETECTION | 73 |
Copyright | |
45 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied Arctic Engineering as-welded ASME assessment axial bending cathodic protection Charpy cold deformation corrosion crack growth rate crack propagation crack tip CTOD cycles depth diameter displacement drillpipe elastic electrode equation experimental factor failure fatigue crack growth fatigue strength ferrite finite element fracture mechanics fracture toughness geometry hoop stress hydrogen Ice Class increase load material maximum mbar Mechanics and Arctic method microstructure modulus nitrogen notch obtained Offshore Mechanics offshore structures OMAE operating oxygen parameters pipe pipeline plastic predicted pressure properties ratio region residual stress S-N curve scour sea ice sea water shear shielding gas simulated soil sour crude oil specimens strain rate stress intensity stress range stress relieved surface Table temperature tensile TMCP tubular joints values wall thickness water hammer weld deposit weld metal weld toe welded joints wire yield strength Young's modulus