Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 7, Part 3American Society of Mechanical Engineers, 1988 - Arctic regions |
From inside the book
Results 1-3 of 15
Page 229
... abrasion tests . The mecha- nism of ice abrasion must also be understood in order to judge whether other kinds of concrete such as lightweight aggregate concrete can be used in areas where ice abrasion is a concern . Abrasion Rate The ...
... abrasion tests . The mecha- nism of ice abrasion must also be understood in order to judge whether other kinds of concrete such as lightweight aggregate concrete can be used in areas where ice abrasion is a concern . Abrasion Rate The ...
Page 231
... abrasion rates as a function of fvs dt is : Abrasion rate ( mm / year ) = 0.00114 vs dt + 0.08 where v ice drift velocity in knots s = ice thickness in mm t = time in days For the sake of simplicity and in order to cover the majority of ...
... abrasion rates as a function of fvs dt is : Abrasion rate ( mm / year ) = 0.00114 vs dt + 0.08 where v ice drift velocity in knots s = ice thickness in mm t = time in days For the sake of simplicity and in order to cover the majority of ...
Page 233
... abrasion and deteration factors that affect on concrete sea structures in arctic regions , were studied with laboratory tests . The damage factors were mechan- ical abrasion effect of sea ice , repeated freezing and thawing of concrete ...
... abrasion and deteration factors that affect on concrete sea structures in arctic regions , were studied with laboratory tests . The damage factors were mechan- ical abrasion effect of sea ice , repeated freezing and thawing of concrete ...
Contents
ADVANCED COMPOSITES | 1 |
PAS2m High Performance Prepreg and Composites | 9 |
OFFSHORE TECHNOLOGY GEOTECHNICAL ENGINEERING | 24 |
Copyright | |
39 other sections not shown
Other editions - View all
Common terms and phrases
abrasion accelerated cooled analysis as-welded austenite axial boron brace brittle fracture CGHAZ Charpy Charpy-V chemical composition chord coarse grained concrete Conference on Offshore crack tip CSM CSM CTOD tests CTOD values curves defect dislocations effect electron beam welding fabrication ferrite fiber Figure finite element fracture mechanics fracture toughness fusion line grain coarsened HAZ HAZ toughness heat affected zone heat input hydrogen cracking ICCGHAZ impact increase kJ/mm layup loading low carbon martensite maximum mechanical properties Mechanics and Arctic mid-thickness niobium notch Offshore Mechanics offshore structures Oseberg parameters plastic post weld heat preheat PWHT regions residual stresses sampled solidification cracking specification specimens steel plates stiffeners strain stress concentration stress intensity factor submerged arc welding surface Table temperature tensile test results TMCP transverse tubular joints weld heat treatment weld metal weld toe weldability welded joints welding procedures weldment yield strength