... carried out without preheat . If the acceptance criteria were not met , the test was repeated with an increased preheat , up to the permitted maximum . Post - weld heat treatment , where applicable , was carried out at 600 ° C + 10 ° C ...
... carried out without preheat . If the acceptance criteria were not met , the test was repeated with an increased preheat , up to the permitted maximum . Post - weld heat treatment , where applicable , was carried out at 600 ° C + 10 ° C ...
Page 183
... carried out in accordance with BS 5762. The test temperature was 10 C. The results are presented in table IV . An equivalent program was carried out to demonstrate to the HAZ toughness in simulated extreme PWHT condition . The PWHT ...
... carried out in accordance with BS 5762. The test temperature was 10 C. The results are presented in table IV . An equivalent program was carried out to demonstrate to the HAZ toughness in simulated extreme PWHT condition . The PWHT ...
Page 595
... carried out to DNV requirements . The majority of the work carried out in this phase concerned 100 percent ultrasonic or magnetic particle inspection of all critical field joints before load testing . The acceptance criteria were to AWS ...
... carried out to DNV requirements . The majority of the work carried out in this phase concerned 100 percent ultrasonic or magnetic particle inspection of all critical field joints before load testing . The acceptance criteria were to AWS ...
Contents
ADVANCED COMPOSITES | 1 |
PAS2tm | 9 |
OFFSHORE TECHNOLOGY GEOTECHNICAL ENGINEERING | 24 |
Copyright | |
39 other sections not shown
Other editions - View all
Common terms and phrases
abrasion accelerated cooled analysis as-welded assessment austenite axial boron brace brittle fracture CGHAZ Charpy Charpy-V chemical composition chord coarse grained concrete Conference on Offshore crack tip CTOD tests CTOD values curves defect dislocations effect energy fabrication ferrite fiber Figure finite element fracture mechanics fracture toughness fusion line grain coarsened HAZ HAZ toughness heat affected zone heat input hydrogen cracking ICCGHAZ impact increase intercritically kJ/mm layup loading low carbon martensite maximum mechanical properties Mechanics and Arctic mid-thickness niobium notch Offshore Mechanics offshore structures Oseberg parameters plastic post weld heat preheat pressure PWHT regions residual stresses sampled solidification cracking specification specimens steel plates stiffeners strain stress concentration stress intensity factor submerged arc welding surface Table temperature tensile test results TMCP transverse tubular joints weld heat treatment weld metal weld toe weldability welded joints welding procedures weldment yield strength