... CORROSION FATIGUE FAILURES Corrosion combined with repeated stress is more damaging than either corrosion or fatigue alone . This is substantiated by the " damage ratio " ( corrosion fatigue strength divided by normal fatigue strength ...
... CORROSION FATIGUE FAILURES Corrosion combined with repeated stress is more damaging than either corrosion or fatigue alone . This is substantiated by the " damage ratio " ( corrosion fatigue strength divided by normal fatigue strength ...
Page 463
... corrosion by gaseous H2S . to cause The above references support the author's belief that oxygen or CO2 must be present to promote and to sustain corrosion and provide atomic hydrogen as a product of corrosion to enter into the steel ...
... corrosion by gaseous H2S . to cause The above references support the author's belief that oxygen or CO2 must be present to promote and to sustain corrosion and provide atomic hydrogen as a product of corrosion to enter into the steel ...
Page 472
... corrosion pits , part ' A ' first take place by corrosion , which produce microcrac- ks , and main cracks combined with these pits are next propagated and connected . The fracture surfaces of the specimens ( A , B material and raw ...
... corrosion pits , part ' A ' first take place by corrosion , which produce microcrac- ks , and main cracks combined with these pits are next propagated and connected . The fracture surfaces of the specimens ( A , B material and raw ...
Contents
ADVANCED COMPOSITES | 1 |
PAS2m High Performance Prepreg and Composites | 9 |
OFFSHORE TECHNOLOGY GEOTECHNICAL ENGINEERING | 24 |
Copyright | |
39 other sections not shown
Other editions - View all
Common terms and phrases
abrasion accelerated cooled analysis as-welded austenite axial boron brace brittle fracture CGHAZ Charpy Charpy-V chemical composition chord coarse grained concrete Conference on Offshore crack tip CSM CSM CTOD tests CTOD values curves defect dislocations effect electron beam welding fabrication ferrite fiber Figure finite element fracture mechanics fracture toughness fusion line grain coarsened HAZ HAZ toughness heat affected zone heat input hydrogen cracking ICCGHAZ impact increase kJ/mm layup loading low carbon martensite maximum mechanical properties Mechanics and Arctic mid-thickness niobium notch Offshore Mechanics offshore structures Oseberg parameters plastic post weld heat preheat PWHT regions residual stresses sampled solidification cracking specification specimens steel plates stiffeners strain stress concentration stress intensity factor submerged arc welding surface Table temperature tensile test results TMCP transverse tubular joints weld heat treatment weld metal weld toe weldability welded joints welding procedures weldment yield strength