... cycle was 1400 ° C which made grains coarse . When only a single heat cycle of 1400 ° C in peak temperature is applied , the Charpy absorbed energy at 0 ° C was about 200 J. The second heat cycle of 1000 ° C in peak temperature improved ...
... cycle was 1400 ° C which made grains coarse . When only a single heat cycle of 1400 ° C in peak temperature is applied , the Charpy absorbed energy at 0 ° C was about 200 J. The second heat cycle of 1000 ° C in peak temperature improved ...
Page 516
... cycle ( third cycle ) , metallurgical changes take place on the phase that was formed at low temperature by the preceding cycles , e.g. high - carbon martensitic island . SCGR ICGC Ac3 / 1 A cí SCGC BM WM HAZ FL UAGC Fig . 2 CTOD Value ...
... cycle ( third cycle ) , metallurgical changes take place on the phase that was formed at low temperature by the preceding cycles , e.g. high - carbon martensitic island . SCGR ICGC Ac3 / 1 A cí SCGC BM WM HAZ FL UAGC Fig . 2 CTOD Value ...
Page 520
... cycle with peak temperature between 900 ° C and 1400 ° C , the second thermal cycle with peak temperature of 800 ° C was added . While dt8 / 5 of the first cycle was kept constant at 20sec . , that of the second cycle was set at 2sec ...
... cycle with peak temperature between 900 ° C and 1400 ° C , the second thermal cycle with peak temperature of 800 ° C was added . While dt8 / 5 of the first cycle was kept constant at 20sec . , that of the second cycle was set at 2sec ...
Contents
ADVANCED COMPOSITES | 1 |
PAS2tm | 9 |
OFFSHORE TECHNOLOGY GEOTECHNICAL ENGINEERING | 24 |
Copyright | |
39 other sections not shown
Other editions - View all
Common terms and phrases
abrasion accelerated cooled analysis as-welded assessment austenite axial boron brace brittle fracture CGHAZ Charpy Charpy-V chemical composition chord coarse grained concrete Conference on Offshore crack tip CTOD tests CTOD values curves defect dislocations effect energy fabrication ferrite fiber Figure finite element fracture mechanics fracture toughness fusion line grain coarsened HAZ HAZ toughness heat affected zone heat input hydrogen cracking ICCGHAZ impact increase intercritically kJ/mm layup loading low carbon martensite maximum mechanical properties Mechanics and Arctic mid-thickness niobium notch Offshore Mechanics offshore structures Oseberg parameters plastic post weld heat preheat pressure PWHT regions residual stresses sampled solidification cracking specification specimens steel plates stiffeners strain stress concentration stress intensity factor submerged arc welding surface Table temperature tensile test results TMCP transverse tubular joints weld heat treatment weld metal weld toe weldability welded joints welding procedures weldment yield strength