... PROGRAMME 1. Scope of Programme The three types of steel have been welded and subsequently the fusion line / heat - affected zone been investigated ( all tests / investigations were conducted in the as - welded condition ) . areas have ...
... PROGRAMME 1. Scope of Programme The three types of steel have been welded and subsequently the fusion line / heat - affected zone been investigated ( all tests / investigations were conducted in the as - welded condition ) . areas have ...
Page 163
... Programme In this programme the following variables were involved : ( 1 ) Level of peak temperature ( 2 ) Number of heat cycles ( 3 ) Cooling time from 800 to 500 ° C ( t 8/5 ) ( 4 ) Post - weld heat treatment . figures Heat input ...
... Programme In this programme the following variables were involved : ( 1 ) Level of peak temperature ( 2 ) Number of heat cycles ( 3 ) Cooling time from 800 to 500 ° C ( t 8/5 ) ( 4 ) Post - weld heat treatment . figures Heat input ...
Page 192
... programme and as such retests , programme delays and modifications to working practices ( if required ) can be extremely costly . This is a particular problem with respect to HAZ CTOD test performance which by its nature often requires ...
... programme and as such retests , programme delays and modifications to working practices ( if required ) can be extremely costly . This is a particular problem with respect to HAZ CTOD test performance which by its nature often requires ...
Contents
ADVANCED COMPOSITES | 1 |
PAS2tm | 9 |
OFFSHORE TECHNOLOGY GEOTECHNICAL ENGINEERING | 24 |
Copyright | |
38 other sections not shown
Other editions - View all
Common terms and phrases
abrasion addition analysis applied assessment base behaviour brittle carbon carried Charpy chemical chord compared composition concrete considered cooling critical CTOD curves cycle defect depth developed direction distribution effect element energy Engineering examined fabrication factor failure fatigue crack ferrite Figure fracture fracture mechanics fracture toughness fusion geometry grain growth hardness heat input higher impact increase indicated initiation joint length loading lower material maximum measured Mechanics method microstructures normal notch observed obtained occur offshore structures parameters performed plate position practice present pressure problem procedure production properties PWHT range reduced regions respectively sampled shown shows simulated specification specimens steel steel plates stiffeners strain strength stress structures surface Table temperature tensile thermal thickness toughness treatment tubular joints values weld metal welded joints yield zone