Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 7, Part 3American Society of Mechanical Engineers, 1988 - Arctic regions |
From inside the book
Results 1-3 of 92
Page 11
... PROPERTIES Mechanical properties of PAS - 2 / carbon fiber laminates were determined using either standard ASTM procedures or procedures supplied by various end users . Table III shows a comparison of the room temperature proper- ties ...
... PROPERTIES Mechanical properties of PAS - 2 / carbon fiber laminates were determined using either standard ASTM procedures or procedures supplied by various end users . Table III shows a comparison of the room temperature proper- ties ...
Page 91
... PROPERTIES OF PLATE Table 2 shows the mechanical properties of the plate . Both strength and toughness in the transverse direction satisfied the specified values of API Specification 2W Grade 60. No significant difference in mechanical ...
... PROPERTIES OF PLATE Table 2 shows the mechanical properties of the plate . Both strength and toughness in the transverse direction satisfied the specified values of API Specification 2W Grade 60. No significant difference in mechanical ...
Page 99
... properties of YS 420 and 460MPa class steel plates for Arctic offshore structures . For the purpose of achieving high strength and good toughness of base plates , it is effective to form the fine acicular ferrite structure by means of ...
... properties of YS 420 and 460MPa class steel plates for Arctic offshore structures . For the purpose of achieving high strength and good toughness of base plates , it is effective to form the fine acicular ferrite structure by means of ...
Contents
ADVANCED COMPOSITES | 1 |
PAS2tm | 9 |
OFFSHORE TECHNOLOGY GEOTECHNICAL ENGINEERING | 24 |
Copyright | |
38 other sections not shown
Other editions - View all
Common terms and phrases
abrasion addition analysis applied assessment base behaviour brittle carbon carried Charpy chemical chord compared composition concrete considered cooling critical CTOD curves cycle defect depth developed direction distribution effect element energy Engineering examined fabrication factor failure fatigue crack ferrite Figure fracture fracture mechanics fracture toughness fusion geometry grain growth hardness heat input higher impact increase indicated initiation joint length loading lower material maximum measured Mechanics method microstructures normal notch observed obtained occur offshore structures parameters performed plate position practice present pressure problem procedure production properties PWHT range reduced regions respectively sampled shown shows simulated specification specimens steel steel plates stiffeners strain strength stress structures surface Table temperature tensile thermal thickness toughness treatment tubular joints values weld metal welded joints yield zone