... sampled is GCHAZ whereas the WI proposal mentioned only that the desired microstructure is sampled within the middle 60 % of the specimen and the test should to maximise the amount attempt of this microstructural region sampled . The ...
... sampled is GCHAZ whereas the WI proposal mentioned only that the desired microstructure is sampled within the middle 60 % of the specimen and the test should to maximise the amount attempt of this microstructural region sampled . The ...
Page 201
... sampled , % Fig.2 . CTOD versus per cent grain coarsened HAZ sampled by fatigue crack in the 50mm thick steel A. ( ) * Assumed within the bulk of the specimen The peak temperature used in the second cycle for the ICGCHAZ simulation was ...
... sampled , % Fig.2 . CTOD versus per cent grain coarsened HAZ sampled by fatigue crack in the 50mm thick steel A. ( ) * Assumed within the bulk of the specimen The peak temperature used in the second cycle for the ICGCHAZ simulation was ...
Page 261
... sampled . However , at higher temperatures it would seem that ' pop - ins ' are achieved when larger amounts of coarse grain are sampled and low toughness fracture can be prevented when only small amounts are present . An effect of ...
... sampled . However , at higher temperatures it would seem that ' pop - ins ' are achieved when larger amounts of coarse grain are sampled and low toughness fracture can be prevented when only small amounts are present . An effect of ...
Contents
ADVANCED COMPOSITES | 1 |
PAS2tm | 9 |
OFFSHORE TECHNOLOGY GEOTECHNICAL ENGINEERING | 24 |
Copyright | |
39 other sections not shown
Other editions - View all
Common terms and phrases
abrasion accelerated cooled analysis as-welded assessment austenite axial boron brace brittle fracture CGHAZ Charpy Charpy-V chemical composition chord coarse grained concrete Conference on Offshore crack tip CTOD tests CTOD values curves defect dislocations effect energy fabrication ferrite fiber Figure finite element fracture mechanics fracture toughness fusion line grain coarsened HAZ HAZ toughness heat affected zone heat input hydrogen cracking ICCGHAZ impact increase intercritically kJ/mm layup loading low carbon martensite maximum mechanical properties Mechanics and Arctic mid-thickness niobium notch Offshore Mechanics offshore structures Oseberg parameters plastic post weld heat preheat pressure PWHT regions residual stresses sampled solidification cracking specification specimens steel plates stiffeners strain stress concentration stress intensity factor submerged arc welding surface Table temperature tensile test results TMCP transverse tubular joints weld heat treatment weld metal weld toe weldability welded joints welding procedures weldment yield strength