... Shown 3 Stiffeners At Saddle & Crowns -3 Stiffeners , Positions Shown Stress Concentration Factor 12 . 102 8 . 15 30 45 60 75 90 Angle Around The Intersection From Crown Unstiffened 1 Stiffener At Saddle 2 Stiffeners , Positions Shown 3 ...
... Shown 3 Stiffeners At Saddle & Crowns -3 Stiffeners , Positions Shown Stress Concentration Factor 12 . 102 8 . 15 30 45 60 75 90 Angle Around The Intersection From Crown Unstiffened 1 Stiffener At Saddle 2 Stiffeners , Positions Shown 3 ...
Page 342
... shown in Fig . 2. Sea water was prepared in the laboratory following ASTM D1141-75 reapproved 1980 , the composition of sea water is given in Table 1 . SPECIMENS Two kinds of specimens were used , center - notched tension specimen and ...
... shown in Fig . 2. Sea water was prepared in the laboratory following ASTM D1141-75 reapproved 1980 , the composition of sea water is given in Table 1 . SPECIMENS Two kinds of specimens were used , center - notched tension specimen and ...
Page 429
... shown in Fig . 4. Although pop - in occurred in some specimens of the bending COD test , the critical COD was plotted at the first fracture stage regardless of the presence or absence of pop - in . As shown in the figure , the fracture ...
... shown in Fig . 4. Although pop - in occurred in some specimens of the bending COD test , the critical COD was plotted at the first fracture stage regardless of the presence or absence of pop - in . As shown in the figure , the fracture ...
Contents
ADVANCED COMPOSITES | 1 |
PAS2m High Performance Prepreg and Composites | 9 |
OFFSHORE TECHNOLOGY GEOTECHNICAL ENGINEERING | 24 |
Copyright | |
39 other sections not shown
Other editions - View all
Common terms and phrases
abrasion accelerated cooled analysis as-welded austenite axial boron brace brittle fracture CGHAZ Charpy Charpy-V chemical composition chord coarse grained concrete Conference on Offshore crack tip CSM CSM CTOD tests CTOD values curves defect dislocations effect electron beam welding fabrication ferrite fiber Figure finite element fracture mechanics fracture toughness fusion line grain coarsened HAZ HAZ toughness heat affected zone heat input hydrogen cracking ICCGHAZ impact increase kJ/mm layup loading low carbon martensite maximum mechanical properties Mechanics and Arctic mid-thickness niobium notch Offshore Mechanics offshore structures Oseberg parameters plastic post weld heat preheat PWHT regions residual stresses sampled solidification cracking specification specimens steel plates stiffeners strain stress concentration stress intensity factor submerged arc welding surface Table temperature tensile test results TMCP transverse tubular joints weld heat treatment weld metal weld toe weldability welded joints welding procedures weldment yield strength