... values , at heat inputs between and 5kJ / mm . Steelmakers A and B conducted repeat chemical analyses on plates used for WT tests and these The values from C values were used in the plot . represent ladle analysis . 4.OkJ / mm ( or ...
... values , at heat inputs between and 5kJ / mm . Steelmakers A and B conducted repeat chemical analyses on plates used for WT tests and these The values from C values were used in the plot . represent ladle analysis . 4.OkJ / mm ( or ...
Page 164
... values at -40 ° C of the parent material are reduced to give average values of 30 J and 20 J at subsurface and quarter thickness positions respectively . Minimum individual values were lower , i.e. 21 J and 10 J. This indicates ...
... values at -40 ° C of the parent material are reduced to give average values of 30 J and 20 J at subsurface and quarter thickness positions respectively . Minimum individual values were lower , i.e. 21 J and 10 J. This indicates ...
Page 261
... value has been achieved using both types but the incidence of low values varied , sometimes being greater for one type and then for the other . Consequently , it seems likely that , at least for notches into a straight sided HAZ , that ...
... value has been achieved using both types but the incidence of low values varied , sometimes being greater for one type and then for the other . Consequently , it seems likely that , at least for notches into a straight sided HAZ , that ...
Contents
ADVANCED COMPOSITES | 1 |
PAS2m High Performance Prepreg and Composites | 9 |
OFFSHORE TECHNOLOGY GEOTECHNICAL ENGINEERING | 24 |
Copyright | |
39 other sections not shown
Other editions - View all
Common terms and phrases
abrasion accelerated cooled analysis as-welded austenite axial boron brace brittle fracture CGHAZ Charpy Charpy-V chemical composition chord coarse grained concrete Conference on Offshore crack tip CSM CSM CTOD tests CTOD values curves defect dislocations effect electron beam welding fabrication ferrite fiber Figure finite element fracture mechanics fracture toughness fusion line grain coarsened HAZ HAZ toughness heat affected zone heat input hydrogen cracking ICCGHAZ impact increase kJ/mm layup loading low carbon martensite maximum mechanical properties Mechanics and Arctic mid-thickness niobium notch Offshore Mechanics offshore structures Oseberg parameters plastic post weld heat preheat PWHT regions residual stresses sampled solidification cracking specification specimens steel plates stiffeners strain stress concentration stress intensity factor submerged arc welding surface Table temperature tensile test results TMCP transverse tubular joints weld heat treatment weld metal weld toe weldability welded joints welding procedures weldment yield strength