... internal corrosion was machined in the rings . The rings were instrumented and pressurised to failure . The results of the pipe ring tests are compared with the predictions of 2 - d elastic - plastic finite element analyses . Particular ...
... internal corrosion was machined in the rings . The rings were instrumented and pressurised to failure . The results of the pipe ring tests are compared with the predictions of 2 - d elastic - plastic finite element analyses . Particular ...
Page 411
... internal coating according to Kut ( Ref . 13 ) . If properly performed , the commissioning is not believed to cause significant deterioration of the internal coating . an no taken In the corrosion assessments for the four scenarios ...
... internal coating according to Kut ( Ref . 13 ) . If properly performed , the commissioning is not believed to cause significant deterioration of the internal coating . an no taken In the corrosion assessments for the four scenarios ...
Page 417
... internal corrosion is expected to Occour during service conditions , but thin film epoxy coating has been specified for the internal coating as an aid for pigging and cleaning and as a flow improver . No coating will be applied to the ...
... internal corrosion is expected to Occour during service conditions , but thin film epoxy coating has been specified for the internal coating as an aid for pigging and cleaning and as a flow improver . No coating will be applied to the ...
Contents
MEASUREMENT AND METERING | 1 |
OFFSHORE PIPELINE TECHNOLOGY | 53 |
CODESSTANDARDS AND REGULATIONS | 75 |
Copyright | |
12 other sections not shown
Other editions - View all
Common terms and phrases
Alberta analysis applied Arctic assessment axial bending buckling calculated calibration construction corrosion crack criteria cylinder damage defects depth developed discharge coefficient displacement distribution downstream effect Engineering environmental equation equipment estimated evaluation experimental failure probability fatigue finite element flow function fluid force fractile fracture fracture mechanics frequency frost heave function gas pipeline hoop stress installation leak detection lift force limit Limit States Design load lognormal longitudinal maximum measured Mechanics meter tube methods nozzle offshore pipelines OMAE operating orifice plate parameters pipe wall pipeline spans pipeline system Pipeline Technology ASME plastic predicted pressure ratio reliability Reynolds number S-N curve sample scour shear stress simulation soil specific standards steel strain structural Table Technology ASME 1992 temperature differential tube bundle turbulent upstream usage factor velocity profile vibration volumetric flow rate vortex shedding wall thickness weld yield strength