Page 39
... indices 12 1 16 3 Miller indices are always cleared of fractions , as shown above . As stated earlier , if a plane is parallel to a given axis , its fractional intercept on that axis is taken as infinity and the corresponding Miller ...
... indices 12 1 16 3 Miller indices are always cleared of fractions , as shown above . As stated earlier , if a plane is parallel to a given axis , its fractional intercept on that axis is taken as infinity and the corresponding Miller ...
Page 40
... indices of a plane in the hexagonal system , called Miller - Bravais indices , refer to four axes and are written ( hkil ) . The index i is the recipro- cal of the fractional intercept on the a3 axis . Since the intercepts of a plane on ...
... indices of a plane in the hexagonal system , called Miller - Bravais indices , refer to four axes and are written ( hkil ) . The index i is the recipro- cal of the fractional intercept on the a3 axis . Since the intercepts of a plane on ...
Page 41
... indices of the zone axis . Such planes may have quite different indices and spacings , the only requirement being their parallelism to a line . Figure 2-12 shows some examples . If the axis of a zone has indices [ uvw ] , then any plane ...
... indices of the zone axis . Such planes may have quite different indices and spacings , the only requirement being their parallelism to a line . Figure 2-12 shows some examples . If the axis of a zone has indices [ uvw ] , then any plane ...
Contents
THE GEOMETRY OF CRYSTALS | 29 |
CHAPTER 3 | 78 |
CHAPTER 4 | 104 |
Copyright | |
21 other sections not shown
Other editions - View all
Common terms and phrases
absorption coefficient absorption edge alloy atomic number austenite axes axis back-reflection Bragg angle Bragg law Bravais lattice calculated camera chart circle composition constant copper cosĀ² counter counting rate cubic curve Debye ring Debye-Scherrer decreases determined diffracted beam diffraction lines diffraction pattern diffractometer direction distance effect electrons elements energy equation error example face-centered face-centered cubic factor film filter given grain hexagonal incident beam indices integrated intensity lattice parameter Laue method martensite measured metal normal obtained orthorhombic parallel percent phase photograph pinhole plotted point lattice pole figure position powder pattern produced pulses rays reciprocal lattice reflecting planes relative rhombohedral rotation sample scaler scattering shown in Fig slit solid solution spacing specimen sphere stereographic projection stress structure substance surface symmetry temperature tetragonal thickness tion transmission twin unit cell vector voltage wave wavelength x-ray beam x-ray diffraction x-ray tube zero zone