274 228 185 177 Base HAZ Weld metal 50 mm SMAW - AW . 254 220 290 286 222 194 182 Base metal HAZ Weld 50 mm SMAW - PWHT 287 197 193 221 Base metal HAZ Weld 50 mm SMAW - AW 247 247 243 193 189 183 185 Base HAZ Weld metal Base metal HAZ Weld ...
274 228 185 177 Base HAZ Weld metal 50 mm SMAW - AW . 254 220 290 286 222 194 182 Base metal HAZ Weld 50 mm SMAW - PWHT 287 197 193 221 Base metal HAZ Weld 50 mm SMAW - AW 247 247 243 193 189 183 185 Base HAZ Weld metal Base metal HAZ Weld ...
Page 633
... base metal , the weld metal and the junction between weld and base plate ( heat affected zone ) when the weldment is subjected to external forces . For examp- le , if some defect / crack is present in amounts or dimensions not easily ...
... base metal , the weld metal and the junction between weld and base plate ( heat affected zone ) when the weldment is subjected to external forces . For examp- le , if some defect / crack is present in amounts or dimensions not easily ...
Page 689
... base metal was investigated by varying the toughness of the base metal . The toughness of the base metal was varied by changing ferrite grain size . 3.1 Experimental Method The chemical composition of the steel is the same as Steel 1 of ...
... base metal was investigated by varying the toughness of the base metal . The toughness of the base metal was varied by changing ferrite grain size . 3.1 Experimental Method The chemical composition of the steel is the same as Steel 1 of ...
Contents
OFFSHORE MECHANICS | 1 |
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Copyright | |
50 other sections not shown
Other editions - View all
Common terms and phrases
alloy aluminum analysis applied Arctic Engineering ASTM austenite axial base metal behaviour bending brace calculated cathodic protection Charpy chord Conference on Offshore corrosion fatigue crack depth crack growth rate crack initiation crack propagation crevice corrosion CTOD da/dN defects developed energy environment equation experimental fabrication fatigue crack growth fatigue strength fatigue test ferrite Figure fillet welds finite element fracture mechanics fracture toughness geometry grade heat input heat treatment HSLA steels increase influence kJ/cm load material mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters pipe pitting plate thickness predicted procedure PWHT ratio reduced S-N curves seawater Shoralsim shown in Fig solution specimens Steel in Marine strain stress concentration stress intensity factor stress range submerged arc welding surface crack T-joints Table temperature tensile thickness effect tubular joints values weld metal weld profile weld toe weldability welded joints yield strength